Ebalta Kunststoff Gmbh AH 140LI 130 2
- Chemical Family
- Epoxy & Epoxy Derivatives
Ebalta AH 140 / LI 130-2 is a general purpose resin.
Product families
Applications
- Consumer Goods — Other Consumer Goods Applications
- Exterior & Body
- Interior
- Other Automotive Applications
Product Families
- Epoxies
Other characteristics
- End Uses
Automotive Applications, Automotive Exterior Parts, Automotive Interior Parts, General Purpose
- Polymer Name
- Epoxy Resins & Compounds
- Flexural Strength
- 107.0 - 127.0 MPa
- Markets
- Automotive & Transportation
- Consumer Goods
- Storing
At appropriate storage 18-25°C.; Occuring crystallization due to disadvantageous storage conditions can be made return by warming up the material at approx. 60° C for some hours.; Opened containers should be closed immediately after use and be protected against moisture. This material should be used up as soon as possible.; Shelf life is indicated on the labels
- Properties
cures tack free high heat resistance long processing time
- Cure
- Chemical Cure
- Technology
- Plastics
- Material Features
- General Purpose
- Very Good Heat Resistance
- Package Unit
Resin AH 140 5,000 kg / 10,000 kg / 25,000 kg / 50,000 kg / 220,000 kg; hardener LI 130-2 3,500 kg
- Processing Instruction
The temperature of material and processing should be between 18 and 25° C.; The mixing of resin and hardener should be made intensively and if possible without any bubbles at room temperature.; We recommend a post curing with a temperature rise of about 10°C/hour. Difficult geometries should be supported during the curing cycle. Afterwards the part should be cooled down at about 20°C/hour.
- Plastics and Elastomers End Uses
- Automotive Applications
- Automotive Exterior Parts
- Automotive Interior Parts
- General Purpose
- Plastics and Elastomers Functions
- Resin
Technical data
Table 1 of 1
15 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Shore hardness | 85 ± 2 | Shore D | DIN ISO 7619-1 |
| Viscosity (25°C) | 550 ± 75 | mPa.s | — |
| Compressive Strength | 95 ± 5 | MPa | EN ISO 604 |
| Density (20°C) | 1,12 ± 0,02 | g/cm3 | — |
| Flexural elongation at break | 7.5 ± 0.3 | % | EN ISO 178 |
| Pot Life (200g/20°C) | 120 - 140 | minutes | — |
| Flexural modulus | 2860 ± 250 | MPa | EN ISO 178 |
| Curing time at RT | 40 - 48 | Hrs | — |
| Flexural strength | 117 ± 10 | MPa | EN ISO 178 |
| Post Curing | 4 ( 60+) | Time in h (Temperature in °C) | — |
| Post Curing | 6 ( 80+) | Time in h (Temperature in °C) | — |
| Post Curing | 4 ( 120) | Time in h (Temperature in °C) | — |