Ebalta Kunststoff Gmbh AH 110TGL
- Chemical Family
- Epoxy & Epoxy Derivatives
Ebalta AH 110 / TGL is an unfilled epoxy resin with high strength values and dimensional stability, even at increased temperature. It can be used as casting resin with powdered fillers as aluminum powder, laminating resin with glass fabric and binder with grainy fillers as aluminum granules. Depending on application the suitable hardener can be mixed with the resin. AH 110/TGL is suitable as laminating resin for big surfaces at a temperature range until 110 °C.
Product families
Applications
- Consumer Goods — Other Consumer Goods Applications
- Other Building Materials
- Textile Manufacturing
Product Families
- Epoxies
Other characteristics
- End Uses
Construction Applications, General Purpose, Textile Applications
- Polymer Name
- Epoxy Resins & Compounds
- Flexural Strength
- 125.0 - 145.0 MPa
- Basis
- High strength general purpose resin
- Markets
- Building & Construction
- Consumer Goods
- Industrial
- Storing
At appropriate storage 18-25°C. Occuring crystallization due to disadvantageous storage conditions can be made return by warming up the material at approx. 60° C for some hours. Opened containers should be closed immediately after use and be protected against moisture. This material should be used up as soon as possible. Shelf life is indicated on the labels
- Properties
unfilled high strength high heat resistance medium viscosity
- Technology
- Plastics
- Material Features
- General Purpose
- High Strength
- Medium Viscosity
- Very Good Heat Resistance
- Package Unit
- 5,000 kg / 10,000 kg / 50,000 kg / 220,000 kg
- 1 kg / 2,5 kg / 5 kg / 25 kg / 50 kg
- Processing Instruction
The temperature of material and processing should be between 18 and 25° C. The mixing of resin and hardener should be made intensively and if possible without any bubbles at room temperature. We recommend a post curing with a temperature rise of about 10°C/hour. Difficult geometries should be supported during the curing cycle. Afterwards the part should be cooled down at about 20°C/hour.
- Plastics and Elastomers End Uses
- Construction Applications
- General Purpose
- Textile Applications
- Plastics and Elastomers Functions
- Resin
Technical data
Table 1 of 1
13 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Shore hardness | 85 ± 3 | Shore D | DIN ISO 7619-1 |
| Viscosity (25°C) | 1000 ± 150 | mPa.s | — |
| Compressive Strength | 115 ± 10 | MPa | EN ISO 604 |
| Density (20°C) | 1,13 ± 0,02 | g/cm3 | — |
| Flexural elongation at break | 6.3 ± 0.7 | % | EN ISO 178 |
| Pot Life (200g/20°C) | 55 - 65 | minutes | — |
| Flexural modulus | 3300 ± 300 | MPa | EN ISO 178 |
| Curing time at RT | 15 - 18 | Hrs | — |
| Flexural strength | 135 ± 10 | MPa | EN ISO 178 |
| Post Curing | 12-80 | Time in h (Temperature in °C) | — |
| Glass transition temperature TG | approx. 102 | °C | — |
| Heat resistance (HDT) | 101 ± 3 | °C | DIN EN ISO 75 B |