Ebalta Kunststoff Gmbh ebatempPUR 5
- Chemical Family
- Polyurethanes (PU)
Ebalta ebatemp is a high-quality two-component Polyurethane casting resin, which is very suitable for the production of vacuum thermoformed moldings. The fast casting resin, which is filled with very fine aluminum powder is very well castable and after curing very well polishable and workable. With ebatemp vacuum thermoformed moldings can be produced within 1-2 hours, these moldings show a temperature capacity of 80-90°C . Post-curing is not necessary. Material should be carefully stirred up/ shacked before use.
Product families
Applications
- Equipment & Parts
- Tooling & Moldmaking
Product Families
- Polyurethanes
Other characteristics
- Density
- 1600.0 - 1700.0 kg/m³
- End Uses
Foundry Dressings, Molds/Dies/Tools, Power/Other Tools
- Polymer Name
- Polyurethane (unspecified)
- Processing Methods
- Casting
- Basis
- Fast curing casting system for vacuum tools
- Markets
- Industrial
- Storing
Storage at room temperature 18-25 °C.; Opened containers should be closed immediately after use and should be used up as soon as possible.; Shelf life is indicated on the labels.
- Properties
very smooth surface polishable well castable well workable aluminum filled
- Technology
- Plastics
- Fillers Included
- Aluminum
- Package Unit
Packing size B-Pack ebatemp / PUR 5 resin 10 x 1,000 kg / hardener 10 x 0,160 kg = 11,600 kg; Units; Comp. A ebatemp Comp. A 1,000 kg / 8,000 kg; Hardener PUR 5 Comp. B 1,000 kg / 6,000 kg
- Plastics and Elastomers End Uses
- Foundry Dressings
- Molds/Dies/Tools
- Power/Other Tools
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Casting
Technical data
Table 1 of 1
12 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Shore hardness | 80 ± 3 | Shore D | DIN ISO 7619-1 |
| Viscosity (25°C) | 1300 ± 300 | mPa.s | — |
| Compressive Strength | 56 ± 5 | MPa | EN ISO 604 |
| Density (20°C) | 1,65 ± 0,05 | g/cm3 | — |
| Flexural elongation at break | 1.1 ± 0.1 | % | EN ISO 178 |
| Pot Life (200g/20°C) | 4,5 - 5,5 | minutes | — |
| Flexural modulus | 4700 ± 400 | MPa | EN ISO 178 |
| Curing time at RT | 1-2 | Hrs | — |
| Flexural strength | 40 ± 5 | MPa | EN ISO 178 |
| Heat resistance (HDT) | 90 ± 3 | °C | DIN EN ISO 75 B |
| Impact resistance (Charpy) | 4 ± 0.5 | kJ/m2 | EN ISO 179 |
| Linear shrinkage | 0.13 | % | — |