Ebalta Kunststoff Gmbh Silastic RTV 3120
- Chemical Family
- Silicones
SILASTIC™ RTV-3120 are pourable rubber bases that become firm, flexible silicone rubber when cured. There is a choice of three catalysts to select from in order to tailor your working times and cure rates.
Product families
Applications
- Consumer Goods — Other Consumer Goods Applications
- Tooling & Moldmaking
- Other Devices & Assemblies
- Other Packaging & Assembly Applications
- Semiconductor Manufacturing
Product Families
- Silicone Elastomers
Other characteristics
- End Uses
Encapsulant, General Purpose, Mold Making, Semiconductor Applications
- Features
- General Purpose, Low Viscosity
- Polymer Name
- Silicone Elastomer
- Markets
- Consumer Goods
- Electrical & Electronics
- Industrial
- Storage
Product should be stored at or below 32ºC (89.6ºF) in original, unopened containers.
- Usage
Substrate Penetration The surface of the original should be clean and free of loose material. If necessary, and in particular with porous substrates, use a suitable release agent such as petroleum jelly or soap solution.. Mixing Thoroughly stir SILASTIC RTV-3100 Series bases before using, as filler separation may occur upon prolonged standing. Weigh the base and appropriate catalyst into a clean container, mix together until the catalyst is completely dispersed in the base. Hand or mechanical mixing can be used, but do not mix for an extended period of time or allow the temperature to exceed 35°C (95°F). With the exception of SILASTIC RTV-3110 Base, it is strongly recommended that entrapped air be removed in a vacuum chamber, allowing the mix to completely expand and then collapse. A vacuum of at least 28 inches of mercury should be held until most bubbling has ceased. After an additional 1–2 minutes under vacuum, the mix should be inspected and if free of air bubbles, can then be used. A volume increase of 3–5 times will occur on vacuum de-airing the mixtures, so a suitably large container should be chosen.
- Technology
- Elastomers
- Material Features
- General Purpose
- Low Viscosity
- HIGHLIGHTS
Is easily mixed and poured; Cures at room temperature in any thickness; Gives accurate reproduction of masters for moldmaking; Provides a wide service temperature range
- Benefits and Features
Two-part RTV silicone rubbers Low mixed viscosity Adjustable cure times Easy to use Reproduce intricate details Works in a wide range of service temperatures
- Plastics and Elastomers End Uses
- Encapsulant
- General Purpose
- Mold Making
- Semiconductor Applications
Technical data
Table 1 of 1
15 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Viscosity at 25°C (77°F), poise | 130 | mPa.s | — |
| Durometer Hardness | 45 | Shore A | — |
| Viscosity (25°C, 77°F) | 280 | poise | — |
| Durometer Hardness | 56 | Shore A | — |
| Elongation, percent | 170 | — | — |
| Specific Gravity (25°C, 77°F) | 1.45 | — | — |
| Specific gravity at 25°C (77°F) | 1.14 | — | — |
| Useful Temperature Range | -55 to 300 (-67 to 572) | °C (°F) | — |
| Tensile strength | 395 | °C | — |
| Tensile Strength (Die C) | 582 | psi | — |
| Elongation | 128 | % | — |
| Dielectric Constant (100 Hz 25°C, 77°F) | 3.72 | — | ASTM D 150 |