Ebalta Kunststoff Gmbh AH 100TGL
- Chemical Family
- Epoxy & Epoxy Derivatives
Ebalta AH 100 is a very thin, unfilled epoxy resin, which can be used with different hardeners. Depending on the application the suitable hardener can be mixed with the resin AH 100. AH 100 / TGL is preferentially used for big volume backfillings.
Product families
Applications
- Consumer Goods — Other Consumer Goods Applications
- Other Building Materials
- Textile Manufacturing
Product Families
- Epoxies
Other characteristics
- End Uses
Construction Applications, General Purpose, Textile Applications
- Polymer Name
- Epoxy Resins & Compounds
- Flexural Strength
- 100.0 - 110.0 MPa
- Basis
- Universal gerneral purpose resin
- Markets
- Building & Construction
- Consumer Goods
- Industrial
- Storing
At appropriate storage 18-25°C.; Occuring crystallization due to disadvantageous storage conditions can be made return by warming up the material at approx. 60° C for some hours. Opened containers should be closed immediately after use and be protected against moisture. This material should be used up as soon as possible.; Shelf life is indicated on the labels
- Packages
5,000 kg / 10,000 kg / 25,000 kg / 50,000 kg / 220,000 kg 1 kg / 2,5 kg / 5 kg / 25 kg / 50 kg
- Properties
- unfilled slow curing
- Cure
- Chemical Cure
- Technology
- Plastics
- Material Features
- General Purpose
- Processing Instruction
The temperature of material and processing should be between 18 and 25° C.; The mixing of resin and hardener should be made intensively and if possible without any bubbles at room temperature. We recommend a post curing with a temperature rise of about 10°C/hour.; Difficult geometries should be supported during the curing cycle. Afterwards the part should be cooled down at about 20°C/hour.
- Plastics and Elastomers End Uses
- Construction Applications
- General Purpose
- Textile Applications
- Plastics and Elastomers Functions
- Resin
Technical data
Table 1 of 1
11 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Shore hardness | 87 ± 3 | Shore D | DIN ISO 7619-1 |
| Compressive Strength | 100 ± 8 | MPa | EN ISO 604 |
| Viscosity (25°C) | 550 ± 100 | mPa.s | — |
| Flexural elongation at break | 4.7 ± 0.5 | % | EN ISO 178 |
| Density (20°C) | 1,12 ± 0,02 | g/cm3 | — |
| Flexural modulus | 3000 ± 200 | MPa | EN ISO 178 |
| Pot Life (200g/20°C) | 65 - 75 | minutes | — |
| Flexural strength | 105 ± 5 | MPa | EN ISO 178 |
| Curing time at RT | 18 - 20 | Hrs | — |
| Heat resistance (HDT) | 76 ± 2 | °C | DIN EN ISO 75 B |
| Impact resistance (Charpy) | 37 ± 10 | kJ/m2 | EN ISO 179 |