Ebalta Kunststoff Gmbh GM 968 Comp. A+B
- Chemical Family
- Polyurethanes (PU)
This product is a Polyurethane system If the product is cured at room temperature, no entire chemical and mechanical load before 7 days after curing.
Product families
Applications
- Consumer Goods — Appliances & Electronics
- Consumer Goods — Housewares
- Consumer Goods — Sports & Recreation
- Cooling & Climate
- Fuel Systems
- Interior
- Tires
- Other Industrial Applications
- Tooling & Moldmaking
- Consumer Electronics
- Tubing & Fluids Handling
Product Families
- Polyurethanes
Other characteristics
- Density
- 1020.0 - 1060.0 kg/m³
- End Uses
- Flexible Grips, Mold Making, Tires, Tubing
- Polymer Name
- Polyurethane (unspecified)
- Tensile Strength
- 4.2 - 5.8 MPa
- Processing Methods
- Casting
- Basis
- Flexible casting resin
- Markets
- Automotive & Transportation
- Consumer Goods
- Electrical & Electronics
- Healthcare & Pharma
- Industrial
- Storing
Storage at room temperature 18-25 °C. Opened containers should be closed immediately after use and should be used up as soon as possible. Shelf life is indicated on the labels.
- Properties
shore A hardness 55 very low water absorption excellent flow properties good tear propagation resistance RoHS conform
- Technology
- Plastics
- Material Features
- Excellent Flow Properties
- Good Tear Strength
- Low Absorption
- Package Unit
- Comp. A GM 968 Comp. A 5,000 kg
- Comp. B GM 968 Comp. B 4,000 kg
- Processing Instruction
1. Stir comp.A thoroughly before use 2. To get a product free from bubbles, we recommend degassing of max. 10 min. 3. Molds have to be moisture free 4. In case of use as concrete mold, hydrocarbon-based release agents lead to accelerated aging of the PUR-mold. Material- and processing temperature should be between 18-25°C. Close containers carefully after use. Please follow instructions regarding mixing ratio of resin and hardener. Any resin residues at stirring rods can be cleaned easily with ebaclean
- Certifications and Compliance
- RoHS Compliant
- Plastics and Elastomers End Uses
- Flexible Grips
- Mold Making
- Tires
- Tubing
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Casting
Technical data
Table 1 of 1
10 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| water absorption 35 - 40°C 63 d | 2 | % | — |
| Viscosity (25°C) | 1500 ± 350 | mPa.s | — |
| Elongation at break / test piece type 2 | 700 ± 200 | % | ISO 37 |
| Density (20°C) | 1,04 ± 0,02 | g/cm3 | — |
| Shore hardness | 55 ± 3 | Shore A | DIN ISO 7619-1 |
| Pot Life (200g/20°C) | 25 - 35 | minutes | — |
| Tear resistance arch shaped test piece with incision 1 mm | 16 ± 1 | kN/m | DIN ISO 34-1 |
| Curing time at RT | 20 - 24 | Hrs | — |
| Tear resistance arch shaped test piece without incision | 36 ± 3 | kN/m | DIN ISO 34-1 |
| Tensile strength | 5.0 ± 0.8 | MPa | ISO 37 |