Ebalta Kunststoff Gmbh GM 971 85Comp. A+B
- Chemical Family
- Polyurethanes (PU)
This product is a polyurethane system. Mechanical data according to test pieces post-cured for 8 hrs. at 80°C. No heavy chemical and mechanical stress before 7 days after curing at room temperature (20-23°C).
Product families
Applications
- Consumer Goods — Appliances & Electronics
- Consumer Goods — Housewares
- Consumer Goods — Sports & Recreation
- Cooling & Climate
- Fuel Systems
- Interior
- Tires
- Interior Fixtures
- Other Industrial Applications
- Tooling & Moldmaking
- Consumer Electronics
- Tubing & Fluids Handling
Product Families
- Polyurethanes
Other characteristics
- Density
- 1090.0 - 1130.0 kg/m³
- End Uses
- Flexible Grips, Mold Making, Tires, Tubing
- Polymer Name
- Polyurethane (unspecified)
- Tensile Strength
- 14.0 - 18.0 MPa
- Processing Methods
- Casting
- Basis
- Flexible casting resin
- Markets
- Automotive & Transportation
- Building & Construction
- Consumer Goods
- Electrical & Electronics
- Healthcare & Pharma
- Industrial
- Storing
Storage at room temperature 18-25 °C. Opened containers should be closed immediately after use and should be used up as soon as possible. Shelf life is indicated on the labels.
- Technology
- Plastics
- Material Features
- Flexible
- High Strength
- Mercury Free
- Package Unit
Packing size B-Pack GM 971-85 / Comp. A+B resin 9 x 0,500 kg + hardener 9 x 0,260 kg = 6,840 kg
- Processing Instruction
Material- and working- temperature: between 18 - 25 °C. Close containers after use. Seal porous mold surfaces first (ebalta mold sealer). For optimum mold releasing we recommend a special release agent (like T1-1), which can be applied easily with a brush or be sprayed. Releasing of the mold 2-3 times, evaporate for about 20 min. after each releasing. Mixing ratio resin/hardener according to instructions. Stirring rods etc. with residual resin can be easily cleaned with ebalta cleaning agent Both components can be easily mixed free from air bubbles in small quantities by hand with a stirring rod or in larger quantities with a spiral stirrer. The processing in a vacuum is also possible. For fast demoulding: Material temperature: 25 – 30 °C Molding temperature: 70 °C Demoulding time: approx. 45 minutes at a mold temperature 70°C and 2 mm thickness
- Plastics and Elastomers End Uses
- Flexible Grips
- Mold Making
- Tires
- Tubing
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Casting
Technical data
Table 1 of 1
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile strength | 16 ± 2 | kN/m | — |
| Density (20°C) | 1,11 ± 0,02 | g/cm3 | — |
| Elongation | 550 ± 50 | — | — |
| Pot Life (200g/20°C) | 4-5 | minutes | — |
| Shore hardness | 90 ± 3 | Shore D | DIN ISO 7619-1 |
| Curing time at RT | 2 - 2,5 | Hrs | — |
| Tear resistance / angle test piece | 55 ± 5 | % | ASTM D 624 B |