Ebalta Kunststoff Gmbh IH 16hardener slow
- Chemical Family
- Epoxy & Epoxy Derivatives
Ebalta IH 16 / hardener slow is a very thin liquid two component epoxy resin with high strength values and high mold resistance. Due to its good soaking and wet-out characteristics the resin/hardener mixture is suitable as infilitration resin for porouse printed parts. The resin/hardener mixture is suitable as an infiltrations resin for porouse printed parts because of its good soaking and wet-out characteristics.
Product families
- Epoxies
Other characteristics
- Polymer Name
- Epoxy Resins & Compounds
- Flexural Strength
- 123.8 - 126.2 MPa
- Processing Methods
- 3D Printing
- Basis
- Infiltration resin for porous parts
- Storing
At appropriate storage 18-25°C. Occuring crystallization due to disadvantageous storage conditions can be made return by warming up the material at approx. 60° C for some hours. Opened containers should be closed immediately after use and be protected against moisture. This material should be used up as soon as possible. Shelf life is indicated on the labels
- Packages
- 0,150 kg / 1,200 kg
- Properties
very low viscosity good wet-out characteristics very long flow paths
- Applications
- Infiltration of printed porous parts
- Availability
At bigger quantities of >500g the working time will be clearly shorte. For ebalta IH 16 are 3 different hardeners available. IH 16 hardener slow: pot life 300 - 400 min. IH 16 hardener fast: pot life 50 - 60 min. IH 16 hardener very fast: pot life 15 - 25 min. (for machine application)
- Technology
- Plastics
- Material Features
- High Strength
- Low Viscosity
- Processing Instruction
The temperature of material and processing should be between 18 and 25° C. The mixing of resin and hardener should be made intensively and at room temperature.
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- 3D Printing
Technical data
Table 1 of 1
11 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Shore hardness | 85 ± 3 | Shore D | DIN ISO 7619-1 |
| Viscosity (25°C) | 250 ± 50 | mPa.s | — |
| Compressive Strength | 95 ± 5 | MPa | EN ISO 604 |
| Density (20°C) | 1,13 ± 0,02 | g/cm3 | — |
| Flexural elongation at break | 5.9 ± 0.1 | % | EN ISO 178 |
| Pot Life (200g/20°C) | 300 - 400 | minutes | — |
| Flexural modulus | 3400 ± 300 | MPa | EN ISO 178 |
| Curing time at RT | 36 - 48 | Hrs | — |
| Flexural strength | 125 ± 1.2 | MPa | EN ISO 178 |
| Heat resistance (HDT) | 79 ± 3 | °C | DIN EN ISO 75 B |
| Impact resistance (Charpy) | 60 ± 6 | kJ/m2 | EN ISO 179 |