Ebalta Kunststoff Gmbh AH 100TGS
- Chemical Family
- Epoxy & Epoxy Derivatives
Ebalta AH 100 is a very thin, unfilled epoxy resin, which can be used with different hardeners. Depending on the application the suitable hardener can be mixed with the resin AH 100. The fast hardener TGS is used for thin laminates and small-volume back fillings.
Product families
Applications
- Consumer Goods — Other Consumer Goods Applications
- Other Building Materials
- Textile Manufacturing
Product Families
- Epoxies
Other characteristics
- End Uses
Construction Applications, General Purpose, Textile Applications
- Polymer Name
- Epoxy Resins & Compounds
- Flexural Strength
- 95.0 - 105.0 MPa
- Basis
- Universal gerneral purpose resin
- Markets
- Building & Construction
- Consumer Goods
- Industrial
- Storing
At appropriate storage 18-25°C.; Occuring crystallization due to disadvantageous storage conditions can be made return by warming up the material at approx. 60° C for some hours.; Opened containers should be closed immediately after use and be protected against moisture. This material should be used up as soon as possible.; Shelf life is indicated on the labels
- Packages
5,000 kg / 10,000 kg / 25,000 kg / 50,000 kg / 220,000 kg 1,000 kg / 2,000 Kg / 5,000 kg / 50,000 kg
- Properties
- unfilled fast curing
- Cure
- Chemical Cure
- Technology
- Plastics
- Material Features
- Fast Curing
- General Purpose
- Processing Instruction
The temperature of material and processing should be between 18 and 25° C.; The mixing of resin and hardener should be made intensively and if possible without any bubbles at room temperature.; We recommend a post curing with a temperature rise of about 10°C/hour. Difficult geometries should be supported during the curing cycle. Afterwards the part should be cooled down at about 20°C/hour.
- Plastics and Elastomers End Uses
- Construction Applications
- General Purpose
- Textile Applications
- Plastics and Elastomers Functions
- Resin
Technical data
Table 1 of 1
11 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Shore hardness | 82 ± 3 | Shore D | DIN ISO 7619-1 |
| Compressive Strength | 75 ± 5 | MPa | EN ISO 604 |
| Viscosity (25°C) | 750 ± 100 | mPa.s | — |
| Flexural elongation at break | 6.7 ± 0.5 | % | EN ISO 178 |
| Density (20°C) | 1,12 ± 0,02 | g/cm3 | — |
| Flexural modulus | 2800 ± 200 | MPa | EN ISO 178 |
| Pot Life (200g/20°C) | 25 - 35 | minutes | — |
| Flexural strength | 100 ± 5 | MPa | EN ISO 178 |
| Curing time at RT | 8-10 | Hrs | — |
| Heat resistance (HDT) | 76 ± 3 | °C | DIN EN ISO 75 B |
| Impact resistance (Charpy) | 34 ± 8 | kJ/m2 | EN ISO 179 |