BRALEN+ FB 2-51
- Chemical Family
- PolyethylenesPolyolefins
BRALEN+ FB 2-51 is a film grade of low density polyethylene containing slip agent erucamide and antiblocking agent.
Product families
Applications
- Industrial & Transport Packaging
Product Families
- Polyolefins
Other characteristics
- Brand
- BRALEN+
- Polymer Name
- Low Density Polyethylene (LDPE)
- Additives Included
- Anti-Blocking Agent, Slip Agent
- Anti-Blocking Agent
- Slip Agent
- Processing Methods
- Extrusion
- Markets
- Printing & Packaging
- Recycling
Polyethylene resins are suitable for recycling using modern recycling methods. In-house production waste should be kept clean to facilitate direct recycling.
- Processing
BRALEN+ FB 2-51 can be used in conventional extrusion machines. Recommended processing temperatures are 160-200 °C.
- Technology
- Plastics
- Packaging Type
- Bags
- Labeling Claims
- Recyclable
- REACH Statement
Polymers are exempt of REACH registration. However, their raw materials which mean monomers and relevant additives have been registered. SLOVNAFT, as. is committed to fully respect legislation and will only use REACH compliant raw materials. At this point in time LDPE BRALEN+ does not contain any substances specifically identified as SVHC at levels greater than 0.1%
- Material Features
- Anti-Blocking
- Recyclable
- Slip
- Storage and Handling
Pellets are packed in 25 kg PE-LD bags and transported on stretch wrapped pallets at eligible load of polymer 1375 kg. Heat treated pallets are available as well. We use adhesive between the bags in order to avoid their slipping. Pay attention to this fact during the removing of the bags from the pallets. The prefered method is to lift the bag at first without rotation. Transportation in a road silo or rail silo is also available.; Since polyethylene is a combustible substance, the fire safety rules applicable for combustible materials in warehouses and store rooms should be observed.; If polymer is stored in conditions of high humidity and fluctuating temperatures, then atmospheric moisture can condense inside the packing. If it happened, it is recommended the pellets to be dried before use. During the storage polyethylene should not be exposed to UV radiation and temperatures above 40°C. Producer does not take responsibility for any damages caused by adverse storage.
- Certifications and Compliance
- REACH Exempt (Europe)
- Plastics and Elastomers End Uses
- Cast Films
- Flexible Packaging
- Heavy Duty Bags
- Pouches Flexible Packaging
- Shrink Wrap
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Extrusion
Technical data
Table 1 of 1
18 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density (23°C) | 923 | kg/m3 | ISO 1183-1 |
| Dart Drop (Film properties tested using 50 µm thick blown film extruded at melt temperature of 200°C and a blow up ratio 2.5:1.) | 130 | g | ISO 7765-1 method A |
| Density (23°C) | 923 | kg/m³ | ISO 1183-1 |
| Dart drop (Film properties tested using 50 µm thick blown film extruded at melt temperature of 200°C and a blow up ratio 2.5:1.) | 130 | g | ISO 7765-1 method A |
| Haze (Film properties tested using 50 µm thick blown film extruded at melt temperature of 200°C and a blow up ratio 2.5:1.) | 6 | % | ASTM D1003 |
| MFR (190°C/2.16 kg) | 2 | g/10 min | ISO 1133-1 |
| MFR (190 °C, 2.16 kg) | 2 | g/10 min | ISO 1133-1 |
| Hardness | 44 | Shore D | ISO 868 |
| Slip Agent Erucamide | 500 | ppm | — |
| Slip Agent Erucamide | 500 | ppm | — |
| Tensile Strain at Break (MD, Film properties tested using 50 µm thick blown film extruded at melt temperature of 200°C and a blow up ratio 2.5:1.) | 450 | % | ISO 527-1,3 |
| Tensile Strain at Break (TD, Film properties tested using 50 µm thick blown film extruded at melt temperature of 200°C and a blow up ratio 2.5:1.) | 560 | % | ISO 527-1,3 |