TATREN HF 3 22
- Chemical Family
- PolyolefinsPolypropylenes (PP)
TATREN HF 3 22 is a homopolymer intended for processing on high-speed BOPPF lines. Thanks its special molecular structure it has broad processing window. Produced films have very good stiffness although TATREN HF 3 22 is very elastic during processing. TATREN HF 3 22 contains neither slip nor antiblocking agent. It is calcium stearate free. TATREN HF 3 22 is characterized by very stable and uniform melt flow, very good adhesion to outer layers. It does not break during orienting and has excellent optical properties – low haze and high gloss.
Product families
Applications
- Food & Beverage Packaging
- Film & Foil Coatings
- Film & Foil Coatings
Product Families
- Polyolefins
Other characteristics
- Brand
- TATREN
- Polymer Name
- Polypropylene Homopolymer (HPP)
- Markets
- Paints & Coatings
- Printing & Packaging
- Recycling
Polypropylene resins are suitable for recycling using modern recycling methods. In-house production waste should be kept clean to facilitate direct recycling
- Processing
TATREN HF 3 22 can be processed on standard and also high speed BOPP lines. Recommended processing temperatures are 230 - 240 °C
- Technology
- Plastics
- Packaging Type
- Bags
- Labeling Claims
- Calcium Stearate-free
- Food Contact Acceptable
- Recyclable
- REACH Statement
Polymers are exempt of REACH registration. However, their raw materials which mean monomers and relevant additives have been registered. SLOVNAFT, as. is committed to fully respect legislation and will only use REACH compliant raw materials. At this point in time PP TATREN does not contain any substances specifically identified as SVHC at levels greater than 0.1%.
- Material Features
- Broad Processing Window
- Excellent Elasticity
- Excellent Stiffness
- Good Adhesion
- Good Optical Properties
- High Gloss
- Recyclable
- Storage and Handling
Pellets are packed in 25 kg PE-LD bags and transported on stretch or shrink-wrapped pallets at eligible load of polymer 1375 kg. Heat treated pallets are available as well. We use adhesive between the bags in order to avoid their slipping. Pay attention to this fact during the removing of the bags from the pallets. The preferred method is to lift the bag at first without rotation. Transportation in a road silo or rail silo is also available.; Since polypropylene is a combustible substance, the fire safety rules applicable for combustible materials in warehouses and store rooms should be observed.; If polymer is stored in conditions of high humidity and fluctuating temperatures, then atmospheric moisture can condense inside the packing. If it happened, it is recommended the pellets to be dried before use. During the storage polypropylene should not be exposed to UV radiation and temperatures above 40°C. Producer does not take responsibility for any damages caused by adverse storage.
- Certifications and Compliance
- REACH Exempt (Europe)
- Plastics and Elastomers End Uses
- Flexible Packaging
- Plastics and Elastomers Functions
- Resin
Technical data
Table 1 of 1
12 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus | 1750 | MPa | ISO 178 |
| HDT (0.45 MPa, Flatwise) | 97 | °C | ISO 75-1,2 |
| Izod Impact Strength (notched, -20 °C) | 6 | kJ/m² | ISO 180/A |
| Izod Impact Strength (Notched, -20 °C) | 6 | kJ/m² | ISO 180/A |
| MFR (230°C/2.16 kg) | 3 | g/10 min | ISO 1133-1 |
| MFR (230 °C, 2.16 kg) | 3 | g/10 min | ISO 1133-1 |
| Modulus of Elasticity in Tension | 1700 | MPa | ISO 527-1,2 |
| Rockwell Hardness | 100 | R scale | ISO 2039-2 |
| HDT (0.45 MPa, flatwise) | 97 | °C | ISO 75-1,2 |
| Tensile Strain at Yield | 10 | % | ISO 527-1,2 |
| Tensile Stress at Yield | 35 | MPa | ISO 527-1,2 |
| Tensile Stress at yield | 35 | MPa | ISO 527-1,2 |