TATREN HM 50 46

Chemical Family: PolyolefinsPolypropylenes (PP)

TATREN HM 50 46 is a controlled rheology homopolymer of high fluidity and narrow molecular weight distribution. This grade contains nucleating and antistatic agent. TATREN HM 50 46 is characterized by very good mechanical properties, good dimensional stability and excellent stiffness. It has higher crystallization temperature which allows good de-molding at higher temperature and shorter molding cycles.

Product families

Applications

Consumer Goods — Furniture
Consumer Goods — Housewares
Consumer Goods — Lawn & Garden

Printing & Packaging — Packaging

Food & Beverage Packaging
Healthcare Packaging
Industrial & Transport Packaging
Non-Food Consumer Packaging

Product Families

Plastics — Basic Thermoplastics

Polyolefins

Other characteristics

Brand: TATREN
Polymer Name: Polypropylene Homopolymer (HPP)
Additives Included: Anti-Static Agent, Nucleating Agent
Anti-Static Agent
Nucleating Agent
Processing Methods: Injection Molding, Thin Wall Injection Molding
Markets: Consumer Goods
Printing & Packaging
Recycling: Polypropylene resins are suitable for recycling using modern recycling methods. In-house production waste should be kept clean to facilitate direct recycling.
Processing: TATREN HM 50 46 can be processed on standard injection molding machines. Recommended processing temperatures are 190 - 250 °C.
Technology: Plastics
Packaging Type: Bags
Labeling Claims: Food Contact Acceptable
Recyclable
REACH Statement: Polymers are exempt of REACH registration. However, their raw materials which mean monomers and relevant additives have been registered. SLOVNAFT, as. is committed to fully respect legislation and will only use REACH compliant raw materials. At this point in time PP TATREN does not contain any substances specifically identified as SVHC at levels greater than 0.1%.
Material Features: Anti-Static
Dimensional Stability
Excellent Stiffness
General Purpose
Good Fluidity
Good Mechanical Properties
Narrow Molecular Weight Distribution
Nucleated
Storage and Handling: Pellets are packed in 25 kg PE-LD bags and transported on stretch or shrink-wrapped pallets at eligible load of polymer 1375 kg. Heat treated pallets are available as well. We use adhesive between the bags in order to avoid their slipping. Pay attention to this fact during the removing of the bags from the pallets. The preferred method is to lift the bag at first without rotation. Transportation in a road silo or rail silo is also available.; Since polypropylene is a combustible substance, the fire safety rules applicable for combustible materials in warehouses and store rooms should be observed.; If polymer is stored in conditions of high humidity and fluctuating temperatures, then atmospheric moisture can condense inside the packing. If it happened, it is recommended the pellets to be dried before use. During the storage polypropylene should not be exposed to UV radiation and temperatures above 40°C. Producer does not take responsibility for any damages caused by adverse storage.
Certifications and Compliance: REACH Exempt (Europe)
Plastics and Elastomers End Uses: Caps
Closures
Containers
Cosmetic Packaging
Furniture
General Purpose
Lids
Rigid Films
Plastics and Elastomers Functions: Resin
Plastics and Elastomers Processing Methods: Injection Molding
Thin Wall Injection Molding

Technical data

Table 1 of 1

12 rows

Characteristic	Value	Unit	Method
Flexural Modulus	1850	MPa	ISO 178
HDT (0.45 MPa, Flatwise)	100	°C	ISO 75-1,2
Izod Impact Strength (Notched, -20 °C)	3	kJ/m²	ISO 180/A
Izod Impact Strength (notched, -20 °C)	3	kJ/m²	ISO 180/A
MFR (230°C/2.16 kg)	50	g/10 min	ISO 1133-1
MFR (230 °C, 2.16 kg)	50	g/10 min	ISO 1133-1
Modulus of Elasticity in Tension	1900	MPa	ISO 527-1,2
Rockwell Hardness	106	R scale	ISO 2039-2
HDT (0.45 MPa, flatwise)	100	°C	ISO 75-1,2
Tensile Strain at Yield	8	%	ISO 527-1,2
Tensile Stress at Yield	36	MPa	ISO 527-1,2
Tensile Stress at yield	36	MPa	ISO 527-1,2