TATREN IM 25 75
- Chemical Family
- PolyolefinsPolypropylenes (PP)
TATREN IM 25 75 is a controlled rheology impact copolymer of good fluidity, excellent impact resistance at room temperature, very good impact resistance at minus temperatures and improved stiffness. This grade contains nucleating and antistatic agent.
Product families
Applications
- Consumer Goods — Luggage & Leather Goods
- Consumer Goods — Sports & Recreation
- Exterior & Body
- Food & Beverage Packaging
- Industrial & Transport Packaging
Product Families
- Polyolefins
Other characteristics
- Brand
- TATREN
- Polymer Name
- Polypropylene Impact Copolymer (ICP)
- Additives Included
- Anti-Static Agent, Nucleating Agent
- Anti-Static Agent
- Nucleating Agent
- Processing Methods
- Injection Molding
- Markets
- Automotive & Transportation
- Consumer Goods
- Printing & Packaging
- Recycling
Polypropylene resins are suitable for recycling using modern recycling methods. In-house production waste should be kept clean to facilitate direct recycling.
- Processing
TATREN IM 25 75 can be processed on standard injection molding machines. Recommended processing temperatures are 190 - 250°C.
- Technology
- Plastics
- Packaging Type
- Bags
- Labeling Claims
- Food Contact Acceptable
- Recyclable
- REACH Statement
Polymers are exempt of REACH registration. However, their raw materials which mean monomers and relevant additives have been registered. SLOVNAFT, a.s. is committed to fully respect legislation and will only use REACH compliant raw materials. At this point in time PP TATREN does not contain any substances specifically identified as SVHC at levels greater than 0.1%.
- Material Features
- Anti-Static
- Good Fluidity
- Good Impact Strength
- Impact Resistance
- Low Temperature Impact Resistance
- Nucleated
- Recyclable
- Stiffness
- Storage and Handling
Pellets are packed in 25 kg PE-LD bags and transported on stretch or shrink-wrapped pallets at eligible load of polymer 1375 kg. Heat treated pallets are available as well. We use adhesive between the bags in order to avoid their slipping. Pay attention to this fact during the removing of the bags from the pallets. The preferred method is to lift the bag at first without rotation. Transportation in a road silo or rail silo is also available.; Since polypropylene is a combustible substance, the fire safety rules applicable for combustible materials in warehouses and store rooms should be observed.; If polymer is stored in conditions of high humidity and fluctuating temperatures, then atmospheric moisture can condense inside the packing. If it happened, it is recommended the pellets to be dried before use. During the storage polypropylene should not be exposed to UV radiation and temperatures above 40°C. Producer does not take responsibility for any damages caused by adverse storage.
- Certifications and Compliance
- REACH Exempt (Europe)
- Plastics and Elastomers End Uses
- Automotive Exterior Parts
- Containers
- Crates
- Luggage
- Pails
- Toys
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 1
14 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus | 1100 | MPa | ISO 178 |
| HDT (0.45 MPa, Flatwise) | 80 | °C | ISO 75-1,2 |
| Izod Impact Strength (notched, -20 °C) | 6 | kJ/m² | ISO 180/A |
| Izod Impact Strength (Notched, -20 °C) | 6 | kJ/m² | ISO 180/A |
| Izod Impact Strength (Notched, -20 °C) | 40 | kJ/m² | ISO 180/A |
| Izod Impact Strength (notched, -20 °C) | 40 | kJ/m² | ISO 180/A |
| MFR (230°C/2.16 kg) | 25 | g/10 min | ISO 1133-1 |
| MFR (230 °C, 2.16 kg) | 25 | g/10 min | ISO 1133-1 |
| Modulus of Elasticity in Tension | 1150 | MPa | ISO 527-1,2 |
| Rockwell Hardness | 52 | R scale | ISO 2039-2 |
| HDT (0.45 MPa, flatwise) | 80 | °C | ISO 75-1,2 |
| Tensile Strain at Yield | 6 | % | ISO 527-1,2 |