TATREN TPO 20 77
- Chemical Family
- Polyolefins
TATREN TPO 20 77 is a controlled rheology extra high impact resistance thermoplastic polyolefin with exceptional impact properties even at low temperatures. It is a grade of medium fluidity and contains nucleating agent. TATREN TPO 20 77 is characterized by exceptionally high impact resistance even at minus temperatures and very good impact/stiffness balance.
Product families
Applications
- Interior
Product Families
- Thermoplastic Olefin Elastomers (TPO)
Other characteristics
- Brand
- TATREN
- Features
Cost Effective, Good Balance of Properties, High Stiffness, Impact Resistance, Improved Fluidity, Low Temperature Impact Resistance, Recyclable
- Polymer Name
- Thermoplastic Polyolefin (TPO)
- Processing Methods
- Compounding, Injection Molding
- Markets
- Automotive & Transportation
- Recycling
Polypropylene resins are suitable for recycling using modern recycling methods. In-house production waste should be kept clean to facilitate direct recycling.
- Processing
TATREN TPO 20 77 can be processed on standard injection molding machines. Recommended processing temperatures are 190 - 250 °C.
- Technology
- Elastomers
- Packaging Type
- Bags
- Labeling Claims
- Food Contact Acceptable
- Recyclable
- REACH Statement
Polymers are exempt of REACH registration. However, their raw materials which mean monomers and relevant additives have been registered. SLOVNAFT, as. is committed to fully respect legislation and will only use REACH compliant raw materials. At this point in time PP TATREN does not contain any substances specifically identified as SVHC at levels greater than 0.1%.
- Additives Included
- Nucleating Agent
- Material Features
- Cost Effective
- Good Balance of Properties
- High Stiffness
- Impact Resistance
- Improved Fluidity
- Low Temperature Impact Resistance
- Recyclable
- Storage and Handling
Pellets are packed in 25 kg PE-LD bags and transported on stretch or shrink-wrapped pallets at eligible load of polymer 1375 kg. Heat treated pallets are available as well. We use adhesive between the bags in order to avoid their slipping. Pay attention to this fact during the removing of the bags from the pallets. The preferred method is to lift the bag at first without rotation. Transportation in a road silo or rail silo is also available.; Since polypropylene is a combustible substance, the fire safety rules applicable for combustible materials in warehouses and store rooms should be observed.; If polymer is stored in conditions of high humidity and fluctuating temperatures, then atmospheric moisture can condense inside the packing. If it happened, it is recommended the pellets to be dried before use. During the storage polypropylene should not be exposed to UV radiation and temperatures above 40°C. Producer does not take responsibility for any damages caused by adverse storage.
- Certifications and Compliance
- REACH Exempt (Europe)
- Plastics and Elastomers Processing Methods
- Compounding
- Injection Molding
Technical data
Table 1 of 1
16 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus | 850 | MPa | ISO 178 |
| Hardness | 50 | Shore D | ISO 868 |
| HDT (0.45 MPa, Flatwise) | 70 | °C | ISO 75-1,2 |
| Izod Impact Strength (Notched, -20 °C) | 43 | kJ/m² | ISO 180/A |
| Izod Impact Strength (Notched, -20 °C) | 35 | kJ/m² | ISO 180/A |
| Izod Impact Strength (Notched, -20 °C) | min. 10 | kJ/m² | ISO 180/A |
| Izod Impact Strength (notched, -20 °C) | 43 | kJ/m² | ISO 180/A |
| Izod Impact Strength (notched, -20 °C) | 35 | kJ/m² | ISO 180/A |
| Izod Impact Strength (notched, -20 °C) | min. 10 | kJ/m² | ISO 180/A |
| MFR (230°C/2.16 kg) | 20 | g/10 min | ISO 1133-1 |
| MFR (230 °C, 2.16 kg) | 20 | g/10 min | ISO 1133-1 |
| Modulus of Elasticity in Tension | 900 | MPa | ISO 527-1,2 |