EPOXIBOND™ EB-135LP
- Chemical Family
- Epoxy & Epoxy Derivatives
FLASHBOND™ UV-3700F is a filled, low shrinkage, light curing epoxy adhesive that offers low CTE and high bonds strength. UV-3700F cures to a high Tg, rigid polymer with excellent adhesive to metals, ceramics, and glass. This filled system is excellent for when low viscosity systems are not ideal. Due to the variability of different UV/LED light sources, it is suggested that the user test and specify intensity and exposure time. This product will cure in the presence of visible light (400- 415nm).
Product families
Applications
- Consumer Goods — Appliances & Electronics
- Consumer Electronics
- Medical Devices & Assemblies
- Adhesives & Sealants
- Semiconductor Manufacturing
- Optical Fiber & Telecom
Product Families
- Structural Adhesives
Other characteristics
- Brand
- EPOXIBOND
- Cure Method
- Air Dry, Heat Cure
- Product Type
- 2K (2 component) Adhesive, Adhesive
- 2K (2 component) Adhesive
- Adhesive
- Application Area
Electrical Components, Electronic Components, Medical Applications, Medical Devices, Optical Applications, Optoelectronics Devices, Semiconductors; Electrical Components; Electronic Components; Medical Applications; Medical Devices; Optical Applications; Optoelectronics Devices; Semiconductors
- Compatible Substrates & Surfaces
- Glass, Metal, Plastics, Wood
- Markets
- Consumer Goods
- Electrical & Electronics
- Healthcare & Pharma
- Shelf LIfe
- 1 Year
- Cure
- Air Dry
- Heat Cure
- Availability
Packaged in Pint, Quart, Gallon, and 5-Gallon kit size.; Also available in 50cc dual syringe cartridge
- Technology
- Ready-to-Use Products
- Packaging Type
- Cartridges
- Curing
- Recommended Cure
- 3 hours at 65°C
- Alternate Cure
- 24 hours at 25°C
- Safety Information
- For Industrial Use Only
- Practices of good housekeeping, safety and cleanliness should be followed before, during and after use.
- Warning
- Although the system contains low volatility materials, care should be taken in handling. Adequate ventilation of work place and ovens is essential. These materials may cause injury to the skin following prolonged or repeated contact and dermatitis in susceptible individuals. In case of skin contact, wash thoroughly with soap and water. For eyes, flush immediately with plenty of water for at least 10 minutes and seek medical attention. Refer to Material Safety Data Sheet for additional health and safety information.
- Use Instructions
Mix Resin: Hardener – 100:46 grams by weight or 2:1by volume and vacuum degas.; Cure as recommended achieving the desiredproperties.; Typical cured properties were determined usingrecommended cure schedule.; Some difference in properties may occur with thealternate or other cure schedules.
- Shelf Life Storage
One year when stored in unopened containers at an average temperature of 25°C.
- Certifications and Compliance
- ISO 9001
- REACH (Europe)
- RoHS Compliant
- Ready to Use Product Features
- Fast Cure
- Good Bonding Strength
- Good Impact Strength
- Medium Viscosity
- Compatible Substrates and Surfaces
- Glass
- Metal
- Plastics
- Wood
Technical data
Table 1 of 2
15 rows| Characteristic | Value | Unit |
|---|---|---|
| Specific Gravity | 1.1 | — |
| Hardness | 86 | Shore D |
| Lap Shear Strength to Aluminium (at -55°C) | 2300 | psi |
| Lap Shear Strength to Aluminium (at 25°C) | 3100 | psi |
| Lap Shear Strength to Aluminium (at 95°C) | 150 | psi |
| Die Shear Strength | 1800 | psi |
| Refractive Index | 1.54 | — |
| Service Temperature Range | -55 to 125 | °C |
| Glass Transition Temperature (Tg) | min. 70 | °C |
| Coefficient of Linear Thermal Expansion (Below Tg) | 62 | 10⁻⁶/°C |
| Coefficient of Linear Thermal Expansion (Above Tg) | min. 200 | 10⁻⁶/°C |
| Dielectric Strength | 600 | Volts/mil |
Table 2 of 2
6 rows| Characteristic | Value | Unit |
|---|---|---|
| Adhesive | Part A | — |
| Hardener | Part B | — |
| Mix Ratio by Weight (Resin/Hardener) | 100/46 | — |
| Mix Ratio by Volume (Resin/Hardener) | 100/50 | — |
| Mixed Viscosity (at 25°C) | 4,000 - 7,000 | cps |
| Pot Life (at 25°C, 100 grams) | min. 4 | hours |