EPOXIBOND™ EB-119M
- Chemical Family
- Epoxy & Epoxy Derivatives
EPOXIBOND™ EB-109M-11 is a flexible, two components, low viscosity, clear epoxy adhesive for optical, medical, and semiconductor applications. This long working life adhesive can be cured at room temperature or with moderate heat and provides excellent adhesion to glass, quartz, metals, wood and most plastics.
Product families
- Encapsulants
Other characteristics
- Brand
- EPOXIBOND
- Cure Method
- Air Dry, Heat Cure
- Product Type
2K (2 component) Adhesive, Adhesive, Potting Compound; 2K (2 component) Adhesive; Adhesive; Potting Compound
- Application Area
Electronic Components, Interconnect, Medical Applications, Medical Devices, Optical Applications, Optoelectronics Devices, Photonic Devices, Semiconductor Die Attach; Electronic Components; Interconnect; Medical Applications; Medical Devices; Optical Applications; Optoelectronics Devices; Photonic Devices; Semiconductor Die Attach
- Compatible Substrates & Surfaces
- Glass, Metal, Wood
- Note
Typical Cured Properties After Cure : Tested at 25°C unless otherwise indicated
- Markets
- Consumer Goods
- Electrical & Electronics
- Healthcare & Pharma
- Features
- Low Viscosity & long pot life
- High temperature applications
- Tg greater than 100°C
- Color change
- Shelf LIfe
- 1 Year
- Cure
- Air Dry
- Heat Cure
- Technology
- Ready-to-Use Products
- Frozen Adhesive
Thaw premixed frozen adhesive at room temperature for 5-10 minutes. Dispense adhesive and cure at recommended schedules.
- Safety Information
- For Industrial Use Only
- Practices of good housekeeping, safety and cleanliness should be followed before, during and after use
- Warning
- Adequate ventilation of workplace and ovens is essential. Refer to Material Safety Data Sheet (MSDS) for additional health and safety information.
- Use Instructions
Weigh each 100 grams of EB-119M to 5 grams of Hardener EH-42LV-1.; Mix until uniform. Scrape the sides and bottom of container repeatedly during mixing.; Apply to clean bonding surfaces and cure as recommended to achieve the desired properties.; Typical cured properties were determined using recommended cure schedule.; Some difference in properties may occur with the alternate or other cure schedules.
- Shelf Life Storage
One year when stored in unopened containers at an average temperature of 25°C.
- Packaging And Availability
- 2 parts Kit
- Packaged in Pint, Quart, Gallon, and 5-Gal
- Premixed and frozen
- Packaged in 3cc, 5cc, 10cc and 30cc disposable syringes and ship in dry ice at -80°C
- Certifications and Compliance
- ISO 9001
- REACH (Europe)
- RoHS Compliant
- Ready to Use Product Features
- High Temperature Resistance
- Long Potlife
- Low Viscosity
Technical data
Table 1 of 2
13 rows| Characteristic | Value | Unit |
|---|---|---|
| Specific Gravity | 1.18 | — |
| Hardness | 91 | Shore D |
| Linear Shrinkage | 0.08 | % |
| Lap Shear Strength to Aluminium (at 25°C) | 2000 | psi |
| Lap Shear Strength to Aluminium (at 100°C) | 1300 | psi |
| Service Temperature Range | -55 to 230 | °C |
| Glass Transition Temperature (Tg) | 158 | °C |
| Coefficient of Linear Thermal Expansion (Below Tg) | 38 | 10⁻⁶/°C |
| Coefficient of Linear Thermal Expansion (Above Tg) | 174 | 10⁻⁶/°C |
| Dielectric Strength | 480 | Volts/mil |
| Dielectric Constant (at 1 kHz) | 3.8 | — |
| Dissipation Factor (at 1 kHz) | 0.009 | — |
Table 2 of 2
5 rows| Characteristic | Value | Unit |
|---|---|---|
| Epoxibond | EB-119M | — |
| Hardener | EH-42LV | — |
| Mix Ratio by Weight (Adhesive/Hardener) | 100/5 | — |
| Mixed Viscosity (at 25°C) | 800 - 1200 | cps |
| Pot Life (at 25°C, 100 grams) | min. 8 | hours |