EPOXIBOND™ EB-107LY
- Chemical Family
- Epoxy & Epoxy Derivatives
EPOXIBOND™ EB-107LY is a two-part, low viscosity, clear epoxy adhesive and encapsulating material. EB-107LY is a low yellowing version of EB-107LP-2. It is recommended for bonding and encapsulating where reduced yellowing is preferred. It is recommended for joining transparent materials, such as glass, and where a thin bond line is desired. EB-107LY can be used for bonding most metals, ceramics, and some plastics.
Product families
Applications
- Industrial Adhesives & Sealants
- Industrial Manufacturing
Product Families
- Encapsulants
Other characteristics
- Brand
- EPOXIBOND
- Cure Method
- Air Dry, Heat Cure
- Product Type
- 2K (2 component) Adhesive
- Compatible Substrates & Surfaces
- Ceramic, Glass, Metal, Plastics
- Note
Typical Cured Properties After Recommended Cure : Tested at 25°C unless otherwise indicated
- Markets
- Adhesives & Sealants
- Industrial
- Cure
- Air Dry
- Heat Cure
- Availability
- 2 parts Kit
- Packaged Gallon, and 5-Gallon size.
- Premixed and frozen
- Packaged in 3cc, 5cc, 10cc and 30cc disposable syringes and ship in dry ice at -80°C.
- Technology
- Ready-to-Use Products
- Frozen Adhesive
Thaw premixed frozen adhesive at room temperature for 5-10 minutes. Dispense adhesive and cure at recommended schedules.
- Curing
- Recommended Cure
- 3 hr at 80°C
- Alternate Cure
- 3 days at 25°C
- Safety Information
- For Industrial Use Only
- Practices of good housekeeping, safety and cleanliness should be followed before, during and after use.
- Warning
- Although the system contains low volatility materials, care should be taken in handling. Adequate ventilation of work place and ovens is essential. These materials may cause injury to the skin following prolonged or repeated contact and dermatitis in susceptible individuals. In case of skin contact, wash thoroughly with soap and water. For eyes, flush immediately with plenty of water for at least 10 minutes and seek medical attention. Refer to Material Safety Data Sheet for additional health and safety information.
- Use Instructions
To use, mix, at room temperature, 100 parts by weight of PART A with 35 parts by weight of Part B. Mix until uniform. Vacuum degas the mixture to remove entrapped air for best results. Apply as needed.. Use recommended cure schedule to achieve best performance. Typical cured properties were determined using recommended cure schedule. Some difference in properties may occur with the alternate or other cure schedules.
- Certifications and Compliance
- ISO 9001
- REACH (Europe)
- RoHS Compliant
- Ready to Use Product Features
- Good Non-Yellowing Properties
- Low Viscosity
- Compatible Substrates and Surfaces
- Ceramic
- Glass
- Metal
- Plastics
Technical data
Table 1 of 2
14 rows| Characteristic | Value | Unit |
|---|---|---|
| Specific Gravity | 1.1 | — |
| Hardness | 79 | Shore D |
| Water Absorption (7days Submersion at 25°C) | 0.8 | % |
| Lap Shear Strength to Aluminium | 2100 | psi |
| Flexural Strength (Yield) | 13900 | psi |
| Flexural Modulus (Yield) | 4.4x10⁵ | psi |
| Maximum Service Temperature Range (Continuous) | 150 | °C |
| Maximum Service Temperature Range (Intermittent) * | 200 | °C |
| Glass Transition Temperature (Tg) | 60 | °C |
| Coefficient of Linear Thermal Expansion (From -60°C to 25°C) | 85 | 10⁻⁶/°C |
| Dielectric Constant (at 1 kHz) | 3.9 | — |
| Dissipation Factor (at 1 kHz) | 0.02 | — |
Table 2 of 2
5 rows| Characteristic | Value | Unit |
|---|---|---|
| Epoxibond | Part A | — |
| Hardener | Part B | — |
| Mix Ratio by Weight (Resin/Hardener) | 100/35 | — |
| Mixed Viscosity (at 25°C) | 200 - 300 | cps |
| Pot Life (at 25°C, 100 grams) | min. 8 | hours |