EpoxySet Inc. UB-907FL
- Chemical Family
- Polyurethanes (PU)
UB-907FL is a two-component, industrial grade polyurethane adhesive system. Once cured, it forms a highly flexible bond line which provides peel and shear strength. It is deal for bonding a variety of metals, as well as plastics, glass, wood, and more. Can also be used for potting and encapsulating strain and heat sensitive electronic components.
Product families
Applications
- Consumer Goods — Appliances & Electronics
- Wood Coatings & Finishes
- Adhesives & Sealants
- Potting Compounds
- Glass Coatings
Product Families
- Encapsulants
Other characteristics
- Product Type
- 2K (2 component) Adhesive, Encapsulant
- 2K (2 component) Adhesive
- Encapsulant
- Compatible Substrates & Surfaces
- Glass, Plastics, Wood
- Color
- Blue
- Markets
- Consumer Goods
- Electrical & Electronics
- Paints & Coatings
- Warning
Adequate ventilation of workplace and ovens is essential.
- Shelf LIfe
- 6 Months
- Technology
- Ready-to-Use Products
- Industrial Usage
Product shall be ideally stored in a cool, dry location in unopened containers at a temperature between 8°C to 28°C (46°F to 82°F) unless otherwise labeled. Optimal storage is at the lower half of this temperature range. To prevent contamination of unused product, do not return any material to its original container. For further specific shelf life information, contact your local Technical Service Center.
- Packaging And Availability
- Dual Cartridgs: 50ml, 200ml, 400ml
- Use instructions
To use simply insert the cartridge into the application gun and start the plunger into the cylinders using light pressure on the trigger. Next, remove the cartridge cap and expel a small amount of adhesive to be sure both sides are flowing evenly and freely. If automatic mixing of resin and hardener is desired, attach the mixing nozzle to the end of the cartridge and begin dispensing the adhesive. For hand mixing, expel the desired amount of the adhesive and mix thoroughly. Mix approximately 15 seconds after uniform color is obtained.
- Certifications and Compliance
- ISO 9001
- Ready to Use Product Features
- Flexible
- Good Peeling Strength
- High Flexibility
- High Strength
- Compatible Substrates and Surfaces
- Glass
- Plastics
- Wood
Technical data
Table 1 of 2
8 rows| Characteristic | Value | Unit |
|---|---|---|
| Polyol | Part B | — |
| Isocyanate | PART A | — |
| Mix Ratio by Weight (A:B) | 100/200 | — |
| Mix Ratio by Volume (Part A /Part B) | 1.2 | — |
| Mixed Viscocity (at 25°C) | 200000 | cPs |
| Gel Time (at 25°C, 1/8" bead) | 4 - 7 | minutes |
| Tack Free Time (at 25°C) | 160 - 180 | minutes |
| Recommended Cure (at 25°C) | 24 - 48 | hours |
Table 2 of 2
13 rows| Characteristic | Value | Unit |
|---|---|---|
| Specific Gravity | 1.2 | — |
| Hardness | 45 | Shore D |
| Lap Shear Strength Aluminum (abraded, cured 5 days at 25°C) | 2100 | — |
| Lap Shear Strength Aluminum (anodized, cured 5 days at 25°C) | 750 | — |
| Lap Shear Strength of Stainless Steel (cured 5 days at 25°C) | 1000 | — |
| Lap Shear Strength of Polycarbonate (cured 5 days at 25°C) | 1900 | — |
| Tensile Strength | 1300 | psi |
| T-Peel Strength | 14 | pli |
| Tensile Elongation | 75 | % |
| Water Absorption (7 days immersion at Room Temperature) | 0.14 | % |
| Water Absorption (7 days immersion at 100°C) | 0.98 | % |
| Glass Transition Temperature (Tg) | 45 | °C |