EPOXIBOND™ EB-107LP-2
- Chemical Family
- Epoxy & Epoxy Derivatives
FLASHBOND™ UV-3607HTis a 1-component, UV/Thermal cure adhesive & sealant. This material can cure under moderate intensity UV light as well as elevated temperatures for shadowed areas. Its low viscosity is ideal for coating, capillary action, and doming applications. Unlike traditional dual cure epoxy systems which need light + heat, UV-3607HT can cure either with UV/LED light or with heat.
Product families
- Encapsulants
- Structural Adhesives
Other characteristics
- Brand
- EPOXIBOND
- Cure Method
- Air Dry, Heat Cure
- Product Type
- 2K (2 component) Adhesive, Adhesive
- 2K (2 component) Adhesive
- Adhesive
- Application Area
Interconnect, Medical Devices, Optical Applications, Optoelectronics Devices, Photonic Devices, Semiconductor Die Attach, Semiconductors; Interconnect; Medical Devices; Optical Applications; Optoelectronics Devices; Photonic Devices; Semiconductor Die Attach; Semiconductors
- Compatible Substrates & Surfaces
- Glass, Metal, Plastics, Wood
- Note
Typical Cured Properties : Tested at 25°C unless otherwise indicated
- Markets
- Adhesives & Sealants
- Consumer Goods
- Electrical & Electronics
- Healthcare & Pharma
- Industrial
- Features
Meets USP Class VI biocompatibility standards for medical devices and implantation applications; Adhesion to glass, quartz, metals, wood and most plastics is very good; Ease of use in potting and casting, encapsulation and adhesive.
- Shelf LIfe
- 1 Year
- Cure
- Air Dry
- Heat Cure
- Technology
- Ready-to-Use Products
- Curing
- Recommended Cure
- 3 hrs at 80°C
- Alternate Cure Schedule
- 1-2 days at 25°C
- Safety Information
- For Industrial Use Only
- Practices of good housekeeping, safety and cleanliness should be followed before, during and after use.
- Warning
- Although the system contains low volatility materials, care should be taken in handling. Adequate ventilation of work place and ovens is essential. These materials may cause injury to the skin following prolonged or repeated contact and dermatitis in susceptible individuals. In case of skin contact, wash thoroughly with soap and water. For eyes, flush immediately with plenty of water for at least 10 minutes and seek medical attention. Refer to Material Safety Data Sheet for additional health and safety information.
- Use Instructions
If PART A is solidified or crystallization hasoccurred, heat to 40-50°C until liquid. If full pot life isdesired, let cool to room temperature before use.; Mix 100 grams of Resin, PART-A with 35 grams ofHardener, PART-B and vacuum degas.; Apply to clean bonding surfaces and cure asrecommended to achieve the desired properties.; Typical cured properties were determined usingrecommended cure schedule.; Some difference in properties may occur with thealternate or other cure schedules.
- Shelf Life Storage
The shelf life of these materials is one (1) year when stored in unopened containers at an average temperature of 25°C.
- Certifications and Compliance
- ISO 9001
- REACH (Europe)
- RoHS Compliant
- USP Class VI
- Ready to Use Product Features
- Ease of Handling
- Long Potlife
Technical data
Table 1 of 2
14 rows| Characteristic | Value | Unit |
|---|---|---|
| Specific Gravity | 1.1 | — |
| Hardness | 82 | Shore D |
| Lap Shear Strength to Aluminium | 2300 | psi |
| Service Temperature Range | -55 to 200 | °C |
| Glass Transition Temperature (Tg) | 82 | °C |
| Coefficient of Linear Thermal Expansion (Below Tg) | 61 | 10⁻⁶/°C |
| Coefficient of Linear Thermal Expansion (Above Tg) | min. 150 | 10⁻⁶/°C |
| Dielectric Constant (at 1 kHz) | 4 | — |
| Dissipation Factor (at 1 kHz) | 0.012 | — |
| Volume Resistivity | 1x10¹³ | ohm-cm |
| Refractive Index (at 25°C, 589nm) | 1.53 | — |
| Spectral Transmission (at 320nm) | min. 94 | % |
Table 2 of 2
5 rows| Characteristic | Value | Unit |
|---|---|---|
| Adhesive | Part A | — |
| Hardener | Part B | — |
| Mix Ratio by Weight (Adhesive/Hardener) | 100/35 | — |
| Mixed Viscosity (at 25°C) | 200 - 500 | cps |
| Pot Life (at 25°C, 100 grams) | min. 8 | hours |