EPOXIBOND™ EB-116
- Chemical Family
- Epoxy & Epoxy Derivatives
EPOXIBOND™ EB-107LP-1 is a two component, room temperature curing epoxy featuring very low viscosity, and excellent optical-mechanical properties.
Product families
Applications
- Body Shop & Repair
- Potting Compounds
- Semiconductor Manufacturing
Product Families
- Encapsulants
- Structural Adhesives
Other characteristics
- Brand
- EPOXIBOND
- Cure Method
- Air Dry, Heat Cure
- Product Type
- 2K (2 component) Adhesive, Potting Compound
- 2K (2 component) Adhesive
- Potting Compound
- Application Area
Cryogenic Applications, Electrical Components, Interconnect, Photonic Devices, Printed Electronics, Semiconductors; Cryogenic Applications; Electrical Components; Interconnect; Photonic Devices; Printed Electronics; Semiconductors
- Compatible Substrates & Surfaces
- Ceramic, Glass, Metal, Plastics
- Note
Typical Cured Properties : Tested at 25°C unless otherwise indicated; 1 After 7days, Immersed in water at 100°C; 2 After 7days, Immersed in Isopropanol at Room Temperature; 3 After 7days, In oven at 150°C
- Markets
- Automotive & Transportation
- Electrical & Electronics
- Shelf LIfe
1 Year (Two Parts Kit at 25°C), 1 Year (Frozen at -40°C)
- Cure
- Air Dry
- Heat Cure
- Technology
- Ready-to-Use Products
- Packaging Type
- Cartridges
- Frozen Adhesive
Thaw premixed frozen adhesive at room temperature for 5-10 minutes. Dispense adhesive and cure at recommended schedules.
- Packaging Options
- 2 parts Kit
- Packaged in Pint, Quart, Gallon, and 5-Gallon size. Also available in 50mL and 400mL dual cartridges.
- Premixed and frozen
- Packaged in 3cc, 5cc, 10cc and 30cc disposable syringes and ship in dry ice at -80°C
- Curing
- Recommended Cure
- 2 hr at 65°C
- Alternate Cure
- 24-48 hr at 25°C
- Safety Information
- For Industrial Use Only
- Practices of good housekeeping, safety and cleanliness should be followed before, during and after use.
- Warning
- Adequate ventilation of work place and ovens is essential. These materials may cause injury to the skin following prolonged or repeated contact and dermatitis in susceptible individuals. In case of skin contact, wash thoroughly with soap and water. For eyes, flush immediately with plenty of water for at least 10 minutes and seek medical attention. Refer to Material Safety Data Sheet (MSDS) for additional health and safety information.
- Use Instructions
Weigh each 100 grams of PART-A to 100 grams of Hardener PART-B.; Mix until uniform. Scrape the sides and bottom of container repeatedly during mixing.; Apply to clean bonding surfaces and cure as recommended to achieve the desired properties.; Typical cured properties were determined using recommended cure schedule.; Some difference in properties may occur with the alternate or other cure schedules.
- Certifications and Compliance
- ISO 9001
- REACH (Europe)
- RoHS Compliant
- Ready to Use Product Features
- Excellent Toughness
- Good Peeling Strength
- Good Scratch Resistance
- High Strength
- Impact Resistance
- Improves Physical Properties
- Low Temperature Flexibility
- Low Viscosity
- Compatible Substrates and Surfaces
- Ceramic
- Glass
- Metal
- Plastics
Technical data
Table 1 of 2
14 rows| Characteristic | Value | Unit |
|---|---|---|
| Specific Gravity | 1.1 | — |
| Hardness | 72 | Shore D |
| Lap Shear Strength to Aluminium | 3200 | psi |
| Lap Shear Strength to Aluminium ¹ | 1580 | psi |
| Lap Shear Strength to Aluminium ² | 2330 | psi |
| Lap Shear Strength to Aluminium ³ | 4000 | psi |
| T-peel Strength to Aluminum | 23 | pli |
| Service Temperature Range | -55 to 110 | °C |
| Glass Transition Temperature (Tg) | 50 | °C |
| Coefficient of Linear Thermal Expansion (Below Tg) | 94 | 10⁻⁶/°C |
| Dielectric Strength | 380 | Volts/mil |
| Dielectric Constant (at 1 kHz) | 3.81 | — |
Table 2 of 2
5 rows| Characteristic | Value | Unit |
|---|---|---|
| Adhesive | Part A | — |
| Hardener | Part B | — |
| Mix Ratio by Weight (Adhesive/Hardener) | 100/100 | — |
| Mixed Viscosity (at 25°C) | 5000 - 8000 | cps |
| Pot Life (at 25°C, 100 grams) | 2 | hours |