Toughblend® PBT-1200
- Chemical Family
- Polyesters
Toughblend® PBT-1200 is a glass fiber reinforced compound; offering good mechanical and thermal properties, with additional good chemical resistance.
Properties
- Physical Form
- Pellets
- Solid
Product families
Applications
Automotive & Transportation — Automotive
- Automotive Lighting
- Exterior & Body
- Other Automotive Applications
Industrial — Chemical & Industrial Manufacturing
- Other Industrial Applications
Product Families
Plastics — Engineering & Specialty Polymers
- Polyesters & Copolyesters
Other characteristics
- Brand
- Toughblend
- Polymer Name
- Polybutylene Terephthalate (PBT)
- Fillers Included
- Glass Fiber
- Flexural Modulus
- 4100.0 - 4100.0 MPa
- Processing Methods
- Injection Molding
- Usage
- Automotive applications
- Industrial parts
- Markets
- Automotive & Transportation
- Industrial
- Features
- Glass Fiber Reinforcement, 10%
- Good chemical resistance
- Good mechanical properties
- Good thermal properties
- Flame Rating
- UL 94 HB
- Technology
- Plastics
- Processing Method
- Injection Molding
- Material Features
- Chemical Resistant
- Good Mechanical Properties
- Certifications and Compliance
- UL 94
- Plastics and Elastomers End Uses
- Automotive Applications
- Handles
- Headlight Cover
- Industrial Parts
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 4
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Strength | 87 | MPa | ASTM D638 |
| Tensile Elongation Break | 4.5 | % | ASTM D638 |
| Flexural Modulus | 4100 | MPa | ASTM D790 |
| Flexural Strength | 135 | MPa | ASTM D790 |
Table 2 of 4
11 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Specific Gravity | 1.38 | g/cm3 | ASTM D792 |
| Molding Shrinkage (3.2 mm) | 0.30 - 0.60 | % | ASTM D955 |
| Notched Izod Impact (23°C) | 55 | J/m | ASTM D256 |
| Drying Temperature | 120 | °C | — |
| Drying Time | 4 - 6 | hr | — |
| Rear Temperature | 240 - 245 | °C | — |
| Middle Temperature | 245 - 250 | °C | — |
| Front Temperature | 255 - 260 | °C | — |
| Nozzle Temperature | 255 - 260 | °C | — |
| Processing (Melt) Temp | 240 -260 | °C | — |
| Mold Temperature | 80 -100 | °C | — |
Table 3 of 4
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed, 4.0 mm) | 215 | °C | ASTM D648 |
| Deflection Temperature Under Load (1.82 MPa, Unannealed, 4.0 mm) | 195 | °C | ASTM D648 |
Table 4 of 4
1 row| Characteristic | Value | Method |
|---|---|---|
| Flame Rating (1.6 mm) | HB | UL94 |