To catalogue
Loyblend® YA-1001FR
- Chemical Family
- Acrylonitrile Butadiene Styrene (ABS)PolyestersStyrenics
Loyblend® YA-1001FR is 20% mineral filled flame retardant PBT/ABS polymer alloy compound. This grade offers excellent flame retardancy, low wear and low warping properties. This grade is developed mainly for portable appliances, printer enclosure, electrical electronic applications etc.
Properties
- Physical Form
- Pellets
- Solid
Product families
Applications
Applications
- Consumer Goods — Appliances & Electronics
Building & Construction — Building Materials
- Structural Components
Industrial — Chemical & Industrial Manufacturing
- Equipment & Parts
- Other Industrial Applications
Electrical & Electronics — Devices & Assemblies
- Consumer Electronics
- Other Devices & Assemblies
Electrical & Electronics — Parts & Components
- Housings & Enclosures
- Other Parts & Components
Product Families
Plastics — Engineering & Specialty Polymers
- Blends & Alloys
Other characteristics
- Brand
- Loyblend
- Density
- 1480.0 - 1480.0 kg/m³
- Polymer Name
- PBT/ABS Alloy
- Flexural Modulus
- 5630.0 - 5630.0 MPa
- Tensile Strength
- 52.0 - 52.0 MPa
- Processing Methods
- Injection Molding
- Usage
- Portable appliance
- Electrical/electronic applications
- Printer enclosure
- Business equipment
- Markets
- Building & Construction
- Consumer Goods
- Electrical & Electronics
- Industrial
- Features
- Flame retardant
- Good mechanical properties
- Low wear
- Low warping
- Flame Rating
- UL 94 V0
- Technology
- Plastics
- Fillers Included
- Mineral
- Processing Method
- Injection Molding
- Material Features
- Flame Retardant
- Good Mechanical Properties
- Low Warpage
- Low Wear
- Certifications and Compliance
- UL 94
- Plastics and Elastomers End Uses
- Appliances
- Electrical/Electronic Applications
- Housings
- Machine/Mechanical Parts
- Printer Parts
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 4
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Modulus | 5870 | MPa | ASTM D638 |
| Tensile Strength | 52 | MPa | ASTM D638 |
| Tensile Elongation Break | 5 | % | ASTM D638 |
| Flexural Modulus | 5630 | MPa | ASTM D790 |
| Flexural Strength | 98 | MPa | ASTM D790 |
Table 2 of 4
11 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Specific Gravity | 1.48 | g/cm3 | ASTM D792 |
| Molding Shrinkage (3.2 mm) | 0.40 - 0.60 | % | ASTM D955 |
| Water Absorption - 24hr | 0.15 | % | ASTM D570 |
| Notched Izod Impact (23°C) | 40 | J/m | ASTM D256 |
| Drying Temperature | 80 - 90 | °C | — |
| Drying Time | 4 - 6 | hr | — |
| Rear Temperature | 230 - 240 | °C | — |
| Middle Temperature | 235 - 245 | °C | — |
| Front Temperature | 240 - 250 | °C | — |
| Nozzle Temperature | 250 - 260 | °C | — |
| Mold Temperature | 50 - 90 | °C | — |
Table 3 of 4
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 4.0 mm) | 125 | °C | ASTM D648 |
Table 4 of 4
1 row| Characteristic | Value | Method |
|---|---|---|
| Flame Rating (1.6 mm) | V-0 | UL94 |