Toughblend® PC-1200
- Chemical Family
- Polycarbonate (PC)
Toughblend® PC-1200 is a glass fiber reinforced compound with good surface finish and high rigidity.
Properties
- Physical Form
- Pellets
- Solid
Product families
Applications
Automotive & Transportation — Automotive
- Other Automotive Applications
Building & Construction — Building Materials
- Structural Components
Industrial — Chemical & Industrial Manufacturing
- Equipment & Parts
- Other Industrial Applications
Electrical & Electronics — Devices & Assemblies
- Consumer Electronics
Electrical & Electronics — Parts & Components
- Other Parts & Components
Product Families
Plastics — Engineering & Specialty Polymers
- Polycarbonates
Other characteristics
- Brand
- Toughblend
- Polymer Name
- Polycarbonate (PC)
- Fillers Included
- Glass Fiber
- Flexural Modulus
- 4112.0 - 4112.0 MPa
- Processing Methods
- Injection Molding
- Usage
- Camera components
- Business parts
- Markets
- Automotive & Transportation
- Building & Construction
- Electrical & Electronics
- Industrial
- Features
- Glass Fiber Reinforcement, 10%
- Good surface finish & high rigidity
- Flame Rating
- UL 94 HB
- Technology
- Plastics
- Processing Method
- Injection Molding
- Material Features
- Good Surface Finish
- High Rigidity
- Certifications and Compliance
- UL 94
- Plastics and Elastomers End Uses
- Camera Applications
- Machine/Mechanical Parts
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 4
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Strength | 88 | MPa | ASTM D638 |
| Tensile Elongation Break | 6 | % | ASTM D638 |
| Flexural Modulus | 4112 | MPa | ASTM D790 |
| Flexural Strength | 145 | MPa | ASTM D790 |
Table 2 of 4
11 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Specific Gravity | 1.27 | g/cm3 | ASTM D792 |
| Molding Shrinkage (3.2 mm) | 0.50 - 0.70 | % | ASTM D955 |
| Notched Izod Impact (23°C) | 100 | J/m | ASTM D256 |
| Drying Temperature | 120 | °C | — |
| Drying Time | 4 - 8 | hr | — |
| Rear Temperature | 275 - 280 | °C | — |
| Middle Temperature | 280 - 285 | °C | — |
| Front Temperature | 285 - 295 | °C | — |
| Nozzle Temperature | 295 - 300 | °C | — |
| Processing (Melt) Temp | 275 - 300 | °C | — |
| Mold Temperature | 85 - 110 | °C | — |
Table 3 of 4
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.82 MPa, Unannealed, 4.0 mm) | 138 | °C | ASTM D648 |
Table 4 of 4
1 row| Characteristic | Value | Method |
|---|---|---|
| Flame Rating (1.6 mm) | HB | UL94 |