Mineralblend® PP-1400
- Chemical Family
- PolyolefinsPolypropylenes (PP)
Mineralblend® PP-1400 is a medium flow tale filled homopolymer polypropylene compounds characterized by good impact strength, heat resistance and dimensional stability.
Properties
- Physical Form
- Pellets
- Solid
Product families
Applications
Applications
- Consumer Goods — Appliances & Electronics
Electrical & Electronics — Devices & Assemblies
- Other Devices & Assemblies
Electrical & Electronics — Parts & Components
- Housings & Enclosures
Product Families
Plastics — Basic Thermoplastics
- Polyolefins
Other characteristics
- Brand
- Mineralblend
- Polymer Name
- Polypropylene Homopolymer (HPP)
- Melt Flow Index
- 10.0 - 10.0 g/10 min
- Fillers Included
- Talc
- Processing Methods
- Injection Molding
- Usage
- Appliances Applications
- Electrical / Electronic Parts
- Markets
- Consumer Goods
- Electrical & Electronics
- Features
- Talc Filled, 20%
- Good Impact Strength
- Good Heat Resistance
- Good dimensional stability
- Flame Rating
- UL 94 HB
- Technology
- Plastics
- Processing Method
- Injection Molding
- Material Features
- Dimensional Stability
- Good Impact Strength
- Thermal Shock Resistant
- Certifications and Compliance
- UL 94
- Plastics and Elastomers End Uses
- Appliances
- Electrical/Electronic Applications
- Housings
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 4
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Strength | 34 | MPa | ASTM D638 |
| Tensile Elongation Break | 70 | % | ASTM D638 |
| Flexural Modulus | 2700 | MPa | ASTM D790 |
| Flexural Strength | 57 | MPa | ASTM D790 |
Table 2 of 4
12 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm3 | ASTM D792 |
| Melt Flow Rate (230°C/2.16 kg) | 10 | g/ 10 min | ASTM D1238 |
| Molding Shrinkage (3.2 mm) | 1.00 - 1.40 | % | ASTM D955 |
| Notched Izod Impact (23°C) | 50 | J/m | ASTM D256 |
| Drying Temperature | 100 | °C | — |
| Drying Time | 2 - 4 | hr | — |
| Rear Temperature | 180 - 190 | °C | — |
| Middle Temperature | 190 - 200 | °C | — |
| Front Temperature | 200 - 210 | °C | — |
| Nozzle Temperature | 210 - 220 | °C | — |
| Processing (Melt) Temp | 190 - 220 | °C | — |
| Mold Temperature | 60 - 70 | °C | — |
Table 3 of 4
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed, 4.0 mm) | 124 | °C | ASTM D648 |
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 4.0 mm) | 78 | °C | ASTM D648 |
Table 4 of 4
1 row| Characteristic | Value | Method |
|---|---|---|
| Flame Rating (1.6 mm) | HB | UL94 |