Loyblend® TA-1000
Loyblend® TA-1000 is a general purpose PCIABS polymer alloy. This grade offers high impact resistance, high rigidity and high heat resistance.
Properties
- Physical Form
- Pellets
- Solid
Product families
Applications
Applications
- Consumer Goods — Appliances & Electronics
Automotive & Transportation — Automotive
- Electrical & Electronic Systems
- Other Automotive Applications
Building & Construction — Building Materials
- Structural Components
Industrial — Chemical & Industrial Manufacturing
- Equipment & Parts
- Other Industrial Applications
Electrical & Electronics — Devices & Assemblies
- Automotive Electronics
- Consumer Electronics
- Other Devices & Assemblies
Electrical & Electronics — Parts & Components
- Housings & Enclosures
- Other Parts & Components
Product Families
Plastics — Engineering & Specialty Polymers
- Blends & Alloys
Other characteristics
- Brand
- Loyblend
- Density
- 1150.0 - 1150.0 kg/m³
- Polymer Name
- PC/ABS Alloy
- Flexural Modulus
- 2578.0 - 2578.0 MPa
- Tensile Strength
- 58.0 - 58.0 MPa
- Processing Methods
- Injection Molding
- Usage
- Portable appliances
- Automotive applications
- Electrical/electronic applications
- Business equipment
- Markets
- Automotive & Transportation
- Building & Construction
- Consumer Goods
- Electrical & Electronics
- Industrial
- Features
- High impact resistance
- Good processability
- Good dimensional stability
- High rigidity
- High heat resistance
- Good color stability
- Flame Rating
- UL 94 HB
- Technology
- Plastics
- Processing Method
- Injection Molding
- Material Features
- Dimensional Stability
- Good Color Stability
- Good Processability
- High Rigidity
- Impact Resistance
- Thermal Shock Resistant
- Certifications and Compliance
- UL 94
- Plastics and Elastomers End Uses
- Appliances
- Automotive Applications
- Automotive Electronics
- Electrical/Electronic Applications
- Housings
- Machine/Mechanical Parts
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 4
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Modulus | 2516 | MPa | ASTM D638 |
| Tensile Strength | 58 | MPa | ASTM D638 |
| Tensile Elongation Break | 50 | % | ASTM D638 |
| Flexural Modulus | 2578 | MPa | ASTM D790 |
| Flexural Strength | 97 | MPa | ASTM D790 |
Table 2 of 4
14 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Specific Gravity | 1.15 | g/cm3 | ASTM D792 |
| Rockwell Hardness | 120 | Scale R | ASTM D785 |
| Melt Flow Rate (260°C/5 kg) | 20 | g/ 10 min | ASTM D1238 |
| Melt Flow Rate (260°C/2.16 kg) | 12 | g/ 10 min | ASTM D1238 |
| Molding Shrinkage (3.2 mm) | 0.40 - 0.60 | % | ASTM D955 |
| Water Absorption - 24hr | 0.1 | % | ASTM D570 |
| Notched Izod Impact (23°C) | 755 | J/m | ASTM D256 |
| Drying Temperature | 80 - 90 | °C | — |
| Drying Time | 4 - 6 | hr | — |
| Rear Temperature | 210 - 250 | °C | — |
| Middle Temperature | 220 - 260 | °C | — |
| Front Temperature | 225 - 270 | °C | — |
Table 3 of 4
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed, 4.0 mm) | 132 | °C | ASTM D648 |
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 4.0 mm) | 110 | °C | ASTM D648 |
Table 4 of 4
1 row| Characteristic | Value | Method |
|---|---|---|
| Flame Rating (1.6 mm) | HB | UL94 |