Loyblend® TK-1000
- Chemical Family
- Polycarbonate (PC)PolyestersPolyethylene Terephthalate (PET)
Loyblend® TK-1000 is an impact modified alloy of Polycarbonate and Polyethylene terephthalate polymer. This grade offers good impact resistance. good dimensional stability and high heat resistance.
Properties
- Physical Form
- Pellets
- Solid
Product families
Applications
Automotive & Transportation — Automotive
- Electrical & Electronic Systems
- Exterior & Body
- Interior
- Other Automotive Applications
Electrical & Electronics — Devices & Assemblies
- Automotive Electronics
Product Families
Plastics — Engineering & Specialty Polymers
- Blends & Alloys
Other characteristics
- Brand
- Loyblend
- Density
- 1210.0 - 1210.0 kg/m³
- Polymer Name
- PC/PET Alloy
- Flexural Modulus
- 2390.0 - 2390.0 MPa
- Tensile Strength
- 59.0 - 59.0 MPa
- Processing Methods
- Injection Molding
- Usage
- Automotive exterior / interior parts
- Automotive applications
- Markets
- Automotive & Transportation
- Electrical & Electronics
- Features
- Good impact resistance
- Good dimensional stability
- High heat resistance
- Flame Rating
- UL 94 HB
- Technology
- Plastics
- Processing Method
- Injection Molding
- Material Features
- Dimensional Stability
- Impact Modified
- Impact Resistance
- Thermal Shock Resistant
- Certifications and Compliance
- UL 94
- Plastics and Elastomers End Uses
- Automotive Applications
- Automotive Electronics
- Automotive Exterior Parts
- Automotive Interior Parts
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 4
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Modulus | 2850 | MPa | ASTM D638 |
| Tensile Strength | 59 | MPa | ASTM D638 |
| Tensile Elongation Break | 115 | % | ASTM D638 |
| Flexural Modulus | 2390 | MPa | ASTM D790 |
| Flexural Strength | 92 | MPa | ASTM D790 |
Table 2 of 4
13 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Specific Gravity | 1.21 | g/cm3 | ASTM D792 |
| Rockwell Hardness | 119 | Scale R | ASTM D785 |
| Melt Flow Rate (260°C/2.16 kg) | 15 | g/ 10 min | ASTM D1238 |
| Molding Shrinkage (3.2 mm) | 0.60 - 0.90 | % | ASTM D955 |
| Water Absorption - 24hr | 0.15 | % | ASTM D570 |
| Notched Izod Impact (23°C) | 715 | J/m | ASTM D256 |
| Drying Temperature | 100 - 110 | °C | — |
| Drying Time | 4 - 6 | hr | — |
| Rear Temperature | 230 - 240 | °C | — |
| Middle Temperature | 235 - 245 | °C | — |
| Front Temperature | 240 - 250 | °C | — |
| Nozzle Temperature | 250 - 260 | °C | — |
Table 3 of 4
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 4.0 mm) | 104 | °C | ASTM D648 |
Table 4 of 4
1 row| Characteristic | Value | Method |
|---|---|---|
| Flame Rating (1.6 mm) | HB | UL94 |