Loyblend® HA-1300
Loyblend® HA-1300 is high flow PMMA ABS polymer alloy. This grade offers high hardness, good scratch resistance and excellent weathering resistance with a high gloss surface.
Properties
- Physical Form
- Pellets
- Solid
Product families
Applications
Applications
- Consumer Goods — Appliances & Electronics; Consumer Goods — Other Consumer Goods Applications
Electrical & Electronics — Devices & Assemblies
- Consumer Electronics
- Displays
Product Families
Plastics — Engineering & Specialty Polymers
- Blends & Alloys
Other characteristics
- Brand
- Loyblend
- Density
- 1100.0 - 1100.0 kg/m³
- Polymer Name
- ABS/PMMA Alloy
- Flexural Modulus
- 2644.0 - 2644.0 MPa
- Tensile Strength
- 50.0 - 50.0 MPa
- Processing Methods
- Injection Molding
- Usage
- General purpose
- Home appliance
- LCD frame
- Markets
- Consumer Goods
- Electrical & Electronics
- Features
- High hardness
- Good scratch resistance
- Excellent weathering resistance
- High gloss surface
- Flame Rating
- UL 94 HB
- Technology
- Plastics
- Processing Method
- Injection Molding
- Material Features
- General Purpose
- Good Scratch Resistance
- Good Surface Gloss
- Good Weather Stability
- High Flow
- High Hardness
- Certifications and Compliance
- UL 94
- Plastics and Elastomers End Uses
- Appliances
- Garden Equipment
- General Purpose
- LCD Applications
- Lawn Equipment
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 4
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Modulus | 3000 | MPa | ASTM D638 |
| Tensile Strength | 50 | MPa | ASTM D638 |
| Tensile Elongation Break | 40 | % | ASTM D638 |
| Flexural Modulus | 2644 | MPa | ASTM D790 |
| Flexural Strength | 80 | MPa | ASTM D790 |
Table 2 of 4
12 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Specific Gravity | 1.1 | g/cm3 | ASTM D792 |
| Rockwell Hardness | 115 | Scale R | ASTM D785 |
| Melt Flow Rate (220°C/10 kg) | 30 | g/ 10 min | ASTM D1238 |
| Molding Shrinkage (3.2 mm) | 0.40 - 0.70 | % | ASTM D955 |
| Notched Izod Impact (23°C) | 95 | J/m | ASTM D256 |
| Drying Temperature | 80 - 90 | °C | — |
| Drying Time | 4 - 6 | hr | — |
| Rear Temperature | 190 - 200 | °C | — |
| Middle Temperature | 195 - 205 | °C | — |
| Front Temperature | 200 - 210 | °C | — |
| Nozzle Temperature | 210 - 220 | °C | — |
| Mold Temperature | 50 - 80 | °C | — |
Table 3 of 4
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 4.0 mm) | 76 | °C | ASTM D648 |
Table 4 of 4
1 row| Characteristic | Value | Method |
|---|---|---|
| Flame Rating (1.6 mm) | HB | UL94 |