SOLLAMID B 2700 V0
- Chemical Family
- Polyamides
The SOLLAMID B 2700 V0 features Polyamide 6 Flame Retardant. Presented in natural, black and color in customer pattern.
Product families
Applications
Automotive & Transportation — Automotive
- Other Automotive Applications
- Powertrain & UTH
Building & Construction — Building Materials
- Structural Components
Industrial — Chemical & Industrial Manufacturing
- Equipment & Parts
Electrical & Electronics — Devices & Assemblies
- Automotive Electronics
Electrical & Electronics — Parts & Components
- Other Parts & Components
Product Families
Plastics — Engineering & Specialty Polymers
- Polyamides
Other characteristics
- Brand
- SOLLAMID
- Polymer Name
- Polyamide 6 (PA 6)
- Color
- Black
- Natural
- Other Color
- Markets
- Automotive & Transportation
- Building & Construction
- Electrical & Electronics
- Industrial
- Flame Rating
- UL 94 HB
- Technology
- Plastics
- Main Properties
The Sollamid B 2700 V0 family has mechanical properties and other typical characteristics of Polyamides 6. With anti-flame characteristics: • Excellent Dimensional Stability • High Stiffness • Chemical Inertia • Good Thermal Resistance • Ease of Molding
- Material Features
- Chemical Resistant
- Dimensional Stability
- Flame Retardant
- Good Thermal Stability
- High Stiffness
- Improved Molding Processability
- Self-extinguishing Characteristics
- Certifications and Compliance
- UL 94
- Plastics and Elastomers End Uses
- Bearings
- Gears
- Wear Strip
- Plastics and Elastomers Functions
- Resin
Technical data
Table 1 of 5
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Specific Weight | 1.26 | g/cm³ | ISO 1183 |
| Moisture Absorption (24h-23ºC) | 0.85 | % | — |
Table 2 of 5
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Strength | 125 | MPa | ISO 527 |
| Traction Module | 5500 | MPa | ISO 527 |
| Elongation At Break | 6 | % | ISO 527 |
| Bending Strength | 175 | MPa | ISO 178 |
| Reflection Module | 5800 | MPa | ISO 178 |
| Rockwell Hardness | 120 | Climb | ISO 50802 |
| Notched Charpy-Cp Impact Resistance (23ºC) | 12 | KJ/m² | ISO 180 |
Table 3 of 5
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melting Temperature | 215-220 | ºC | ISO 1218 |
| Continuous Heat Resistance | 90 | ºC | — |
| Deformation Temperature Under Load 1.82 Mpa | min. 150 | ºC | ISO 7512 |
| Deformation Temperature Under Load 0.46 Mpa | min. 190 | ºC | ISO 7512 |
Table 4 of 5
1 row| Characteristic | Value | Unit |
|---|---|---|
| Shrinkage In Molding | 0.80-0.90 | % |
Table 5 of 5
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Volumetric Resistivity | 10 | ohm/cm | ISO CEI93 |
| Dielectric Strength | 18 | Kv/mm | ISO CEI243 |