SOLLAMID A 2700 FV 30 MB 20
- Chemical Family
- Polyamides
The SOLLAMID A 2700 FV 30 MB 20 family features the PA 66 composite reinforced with Fiberglass and Modified with Molybdenum Disulfide.
Product families
Applications
Automotive & Transportation — Automotive
- Other Automotive Applications
Building & Construction — Building Materials
- Structural Components
Industrial — Chemical & Industrial Manufacturing
- Equipment & Parts
- Other Industrial Applications
Product Families
Plastics — Engineering & Specialty Polymers
- Polyamides
Other characteristics
- Brand
- SOLLAMID
- Polymer Name
- Polyamide 66 (PA 66)
- Fillers Included
- Molybdenum Disulfide
- Markets
- Automotive & Transportation
- Building & Construction
- Industrial
- Flame Rating
- UL 94 HB
- Technology
- Plastics
- Main Properties
The Sollamid A FV family has mechanical properties and other characteristics typical of Polyamides 66. • Excellent Dimensional Stability • High Stiffness • Chemical Inertia • Excellent Thermal Resistance • Ease of Molding
- Material Features
- Chemical Resistant
- Dimensional Stability
- Excellent Mechanical Strength
- High Stiffness
- Improved Molding Processability
- Low Friction
- Self Lubricating
- Certifications and Compliance
- UL 94
- Plastics and Elastomers End Uses
- Bushings
- Gears
- Plastics and Elastomers Functions
- Resin
Technical data
Table 1 of 5
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Specific Weight | 1.37 | g/cm³ | ISO D792 |
| Moisture Absorption (24h-23ºC) | 0.8 | % | ISO D570 |
Table 2 of 5
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Linear Expansion Coefficient | 7x10 | 10- 5cm/cm ºC | ISO D696 |
| Tensile Strength | 185 | MPa | ISO D638 |
| Traction Module | 12000 | MPa | ISO D638 |
| Elongation At Break | 4 | % | ISO D638 |
| Bending Strength | 250 | MPa | ISO D790 |
| Reflection Module | 9000 | MPa | ISO D790 |
| Rockwell Hardness | 120 | Climb | ISO D785 |
| Notched Charpy-Cp Impact Resistance (23ºC) | 11 | KJ/m² | ISO D256 |
Table 3 of 5
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melting Temperature | 250-260 | ºC | — |
| Continuous Heat Resistance | 110 | ºC | — |
| Deformation Temperature Under Load 1.82 Mpa | min. 240 | ºC | ISO D648 |
| Deformation Temperature Under Load 0.46 Mpa | min. 240 | ºC | ISO D648 |
Table 4 of 5
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Shrinkage In Molding | 0.3-0.5 | % | ISO D955 |
Table 5 of 5
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Volumetric Resistivity | 10 | ohm/cm | ISO D257 |
| Dielectric Strength | 27 | Kv/mm | ISO D149 |