SOLLAMID AB 2700 FV 50
- Chemical Family
- Polyamides
The SOLLAMID AB 2700 FV 50 Composite characterizes the PA 66/6 reinforced with 50% Fiberglass.
Product families
Applications
Automotive & Transportation — Automotive
- Aftermarket Parts & Components
- Exterior & Body
- Interior
- Other Automotive Applications
Product Families
Plastics — Engineering & Specialty Polymers
- Polyamides
Other characteristics
- Brand
- SOLLAMID
- Polymer Name
- Polyamide 6/66 (PA 6/66)
- Fillers Included
- Glass Fiber
- Markets
- Automotive & Transportation
- Flame Rating
- UL 94 HB
- Technology
- Plastics
- Main Properties
The Sollamid AB FV family has mechanical properties and other characteristics typical of Polyamides 66. • Excellent Dimensional Stability • High Stiffness • Chemical Inertia • Excellent Thermal Resistance • Ease of Molding
- Material Features
- Chemical Resistant
- Dimensional Stability
- Good Mechanical Properties
- Good Surface Finish
- Good Thermal Stability
- High Stiffness
- Improved Molding Processability
- Certifications and Compliance
- UL 94
- Plastics and Elastomers End Uses
- Automotive Components
- Automotive Exterior Parts
- Automotive Interior Parts
- Plastics and Elastomers Functions
- Resin
Technical data
Table 1 of 5
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Strength | 230 | MPa | ASTM 527 |
| Traction Module | 15100 | MPa | ASTM 527 |
| Elongation At Break | two | % | ASTM 527 |
| Bending Strength | 320 | MPa | ASTM 178 |
| Reflection Module | 12100 | MPa | ASTM 178 |
| Rockwell Hardness | 120 | Climb | ASTM 50802 |
| Notched Charpy-Cp Impact Resistance (23ºC) | 17 | KJ/m² | ASTM 180 |
Table 2 of 5
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Specific Weight | 1.26 | g/cm³ | ASTM 1186 |
| Moisture Absorption (24h-23ºC) | 0.65 | % | ASTM 32 |
Table 3 of 5
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melting Temperature | 245-255 | ºC | ASTM 1218 |
| Continuous Heat Resistance | 120 | ºC | — |
| Deformation Temperature Under Load 1.82 Mpa | min. 240 | ºC | ASTM 7512 |
| Deformation Temperature Under Load 0.46 Mpa | min. 240 | ºC | ASTM 7512 |
Table 4 of 5
1 row| Characteristic | Value | Unit |
|---|---|---|
| Shrinkage In Molding | 0.20/0.30 | % |
Table 5 of 5
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Volumetric Resistivity | 10 | ohm/cm | ASTM CEI93 |
| Dielectric Strength | 18 | Kv/mm | ASTM CEI243 |