SOLLAMID A 2700 FV15 V0
- Chemical Family
- Polyamides
The SOLLAMID A 2700 FV15 V0 features Polyamide 66 reinforced with Flame Retardant Fiberglass.
Product families
Applications
Automotive & Transportation — Automotive
- Other Automotive Applications
Building & Construction — Building Materials
- Structural Components
Industrial — Chemical & Industrial Manufacturing
- Equipment & Parts
- Other Industrial Applications
Product Families
Plastics — Engineering & Specialty Polymers
- Polyamides
Other characteristics
- Brand
- SOLLAMID
- Polymer Name
- Polyamide 66 (PA 66)
- Fillers Included
- Glass Fiber
- Markets
- Automotive & Transportation
- Building & Construction
- Industrial
- Flame Rating
- UL 94 V0
- Technology
- Plastics
- Main Properties
The SOLLAMID A 2700 FV15 V0 family has mechanical properties and other characteristics typical of Polyamides 66. With flame retardant properties. • Excellent Dimensional Stability • High Stiffness • Chemical Inertia • Good Thermal Resistance • Ease of Molding
- Material Features
- Chemical Resistant
- Dimensional Stability
- Flame Retardant
- Good Electrical Properties
- Good Mechanical Properties
- High Stiffness
- Improved Molding Processability
- Self Lubricating
- Certifications and Compliance
- UL 94
- Plastics and Elastomers End Uses
- Bushings
- Gears
- Plastics and Elastomers Functions
- Resin
Technical data
Table 1 of 4
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Specific Weight | 1.24 | g/cm³ | ISO 1183 |
| Moisture Absorption (24h-23ºC) | 1.1 | % | — |
Table 2 of 4
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Strength | at 125 | MPa | ISO 527 |
| Traction Module | s 6300 | MPa | ISO 527 |
| Elongation At Break | s 4 | % | ISO 527 |
| Bending Strength | s 165 | MPa | ISO 178 |
| Reflection Module | s 7800 | MPa | ISO 178 |
| Rockwell Hardness | s 120 | Climb | ISO 50802 |
| Izod Cp Notched Impact Resistance | s 6 | KJ/m^{2²} | ISO 180 |
Table 3 of 4
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melting Temperature | 250-260 | ºC | ISO 1218 |
| Continuous Heat Resistance | 110 | ºC | — |
| Deformation Temperature Under Load 1.82 Mpa | min. 240 | ºC | ISO 7512 |
| Deformation Temperature Under Load 0.46 Mpa | min. 240 | ºC | ISO 7512 |
Table 4 of 4
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Volumetric Resistivity | 10 | ohm/cm | ISO CEI93 |
| Dielectric Strength | 18 | Kv/mm | ISO CEI243 |
| Shrinkage In Molding | 0.0-0.70 | % | — |