SOLLAMID AC 9010
- Chemical Family
- Polyamides
Sollamid AC 9010 features low viscosity Polyamide, intended for injection molding.
Product families
Applications
Applications
- Consumer Goods — Appliances & Electronics
- Consumer Goods — Furniture
Automotive & Transportation — Automotive
- Exterior & Body
- Interior
- Other Automotive Applications
Industrial — Chemical & Industrial Manufacturing
- Equipment & Parts
- Other Industrial Applications
Electrical & Electronics — Parts & Components
- Other Parts & Components
Product Families
Plastics — Engineering & Specialty Polymers
- Polyamides
Other characteristics
- Brand
- SOLLAMID
- Polymer Name
- Polyamide (unspecified)
- Processing Methods
- Injection Molding
- Markets
- Automotive & Transportation
- Consumer Goods
- Electrical & Electronics
- Industrial
- Flame Rating
- UL 94 V2
- Technology
- Plastics
- Main Properties
SOLLAMID AC formulas have all the good properties of Polyamide 66 with optimized processability characteristics. • Excellent Impact Resistance • Good Mechanical Properties • Good Thermal Resistance • Chemical Inertia • Ease of Molding
- Material Features
- Chemical Resistant
- Good Mechanical Properties
- Good Thermal Stability
- High Impact Resistance
- Improved Molding Processability
- Low Viscosity
- Certifications and Compliance
- UL 94
- Plastics and Elastomers End Uses
- Appliances
- Automotive Applications
- Automotive Components
- Automotive Exterior Parts
- Automotive Interior Parts
- Furniture
- Machine/Mechanical Parts
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 5
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Specific Weight | 1.14 | g/cm³ | ASTM D792 |
| Moisture Absorption (24h-23ºC) | 1.6 | % | ASTM D570 |
Table 2 of 5
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Linear Expansion Coefficient | 7.0x10-5 | 10- 5cm/cm ºC | ASTM D696 |
| Tensile Strength | 85 | MPa | ASTM D638 |
| Traction Module | 3000 | MPa | ASTM D638 |
| Elongation At Break | 50 | % | ASTM D638 |
| Bending Strength | 125 | MPa | ASTM D790 |
| Bending Modulus | 2900 | MPa | ASTM D790 |
| Rockwell Hardness | 120 | Climb | ASTM D785 |
| Izod Impact Resistance - Notched Cp Two | 6 | KJ/m | ASTM D256 |
Table 3 of 5
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melting Temperature | 240-250 | ºC | — |
| Continuous Heat Resistance | 100 | ºC | — |
| Deformation Temperature Under Load 1.82 Mpa | 70 | ºC | ASTM D648 |
| Deformation Temperature Under Load 0.46 Mpa | 180 | ºC | ASTM D648 |
| Fluidity Index | 10-15 | g/10' | ASTM D1238 |
Table 4 of 5
1 row| Characteristic | Value | Unit |
|---|---|---|
| Shrinkage In Molding | 1.0-1.3 | % |
Table 5 of 5
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Volumetric Resistivity | 10 | ohm/cm | ASTM D257 |
| Dielectric Strength | 21 | Kv/mm | ASTM D149 |