Novolak VEGlaze 472
Novolak VEGlaze 472 is a coating used for the chemical-resistant construction of sumps, ducts, containment areas, trenches, walls, and other support columns or bases. VEGlaze may be used as a thin barrier of corrosion resistance or as a topcoat for other Sauereisen vinyl ester linings and polymer concretes. The VEGlaze system utilizes Sauereisen VEPrime No. 550 as a bond enhancing primer.
Identification
- Chemical Family
- Vinyl Esters, Vinyls, Vinylics & Vinyl Derivatives
Other characteristics
- Brand
- Novolak
- Features
Chemical Resistant, Corrosion Resistant, High Temperature Resistance, Low Porosity
- Product Type
- 2K (2 component) Coating, Top Coat
- 2K (2 component) Coating
- Top Coat
- Application Method
- Gun, Roller, Spray
- Compatible Substrates & Surfaces
- Concrete, Metal, Steel
- Markets
- Industrial
- Paints & Coatings
- Clean Up
All equipment should be cleaned by scrubbing with a stiff brush and MEK or MCT (monochlorotoluene) at the end of each working period or when build-up becomes pronounced.
- Shelf LIfe
Sauereisen VEGlaze No. 472 has a shelf life of three (3) months, when stored in unopened, tightly sealed containers in a dry location at 70°F. Avoid freezing. If there is a doubt as to the quality of the materials, consult a Sauereisen representative.
- Application
VEPrime No. 550 and NovolaK VEGlaze No. 472 are each packaged in premeasured containers consisting of Hardener Part A and Resin Part B which must be mixed together before use. Individual components should be remixed before combining. The following procedures are applicable to the mixing of both products.; Completely empty contents of Hardener Part A into Resin Part B container. Using a slow-speed drill motor with a "Jiffy" type blade, mix for a minimum of three minutes until thoroughly blended.; Mix only complete batches. Material which has begun to set must be discarded. Do not try to retemper the material.
- Cure
- Heat Cure
Technical data
Table 1 of 1
10 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Application Time (Working Time, 70°F) | 30.0 | minutes | — |
| Application Time (Initial Set, 70°F) | 2.0 | hours | — |
| Bond Strength to Concrete | Concrete Failure | — | ASTM D-4541 |
| Components | 2 parts | — | — |
| Maximum Service Temperature (Continuous exposure) | 350.0 | °F | — |
| Maximum Service Temperature (Intermittent or Flue Gas Exposure) | 400.0 | °F | — |
| Thickness (Wet) | 10.0 | mils | — |
| Thickness (Dry) | 7.0 | mils | — |
| VOC Content | 430.0 | g/L | EPA Method 24 |
| Volume Solids | 60.7 | % | — |