Creative Materials 125-01A/B-187
- Chemical Family
- Epoxy & Epoxy Derivatives
125-01A/B-187 is a two-component syringe dispensable, anisotropically conductive, epoxy coating and adhesive. This system features excellent thermal stability, outstanding chemical resistance and excellent high temperature properties. Applications for 125-01A/B-187 include, but are not limited to, conductive splicing of ribbon cables, electrical attachment of surface mounted devices and bonding of flex circuits to PC boards and electroluminescent panels. This product is useful in application where shorts between closely spaced contacts are a concern. This system features excellent thermal stability.\nFeatures
Product families
Applications
- Printed Circuit Boards (PCBs)
Product Families
- Conductive Adhesives
Other characteristics
- Product Type
- Conductive Adhesive, Epoxy Adhesive
- Conductive Adhesive
- Epoxy Adhesive
- Application Area
- Electrical Components, Ribbon Cables
- Electrical Components
- Ribbon Cables
- Application Method
- Injection
- Markets
- Electrical & Electronics
- Shelf LIfe
1 year at ambient temperatures (Part A), 1 year at ambient temperatures (Part B)
- Technology
- Ready-to-Use Products
- Bonding Procedure
To use, carefully align parts to be bonded, apply uniform pressure to maintain location. Follow curing guidelines given above. Timing should start once adhesive and substrate reach curing temperature.
- Curing Guidelines
These temperatures and times are presented as a guide only. The curing times are after substrate has been brought up to temperature. The end-user is encouraged to experiment to determine optimum curing schedule.
- Safety and Handling
Use with adequate ventilation.; Keep away from sparks and open flames.; Avoid prolonged contact with skin and breathing of vapors.; Wash with soap and water to remove from skin
- Application Methods
- Injection
- Handling
Prior to using, mix thoroughly to re-suspend fillers. If needed, 125-01A/B-187 can be thinned with small amounts of Creative Materials' 102-03 thinner. Thinning should be done after mixing parts A and B to maintain proper mixing ratio.
- Certifications and Compliance
- ISO 9001
- Ready to Use Product Features
- Anisotropic
- Chemical Resistant
- Electrically Conductive
- Excellent Coating Performance
- Good Thermal Stability
- High Temperature Resistance
Technical data
Table 1 of 3
5 rows| Characteristic | Value | Unit |
|---|---|---|
| Minimum Cure Temperature | 100 | °C |
| Chloride | max. 10 | ppm |
| Sodium Content | max. 10 | ppm |
| Potassium Content | max. 10 | ppm |
| Pot Life | 4 hours | — |
Table 2 of 3
6 rows| Characteristic | Value | Unit |
|---|---|---|
| Brookfield Viscosity - HAT Viscometer (at 10 rpm at 25°C) | 20000 | cps |
| Specific Gravity | 1.19 | water 1 |
| Filler | Silver | — |
| Percent Silver (cured) | max. 5 | % |
| Theoretical Coverage (0.001" Wet Thickness) | 25 | in^2/gram |
| Solid Content | 71 | N/A |
Table 3 of 3
10 rows| Characteristic | Value | Unit |
|---|---|---|
| Operating Temperature | -55 to +230 | °C |
| Peak Temperature | 325 | °C |
| Volume Resistivity (Z Axis) | 0.001 | Ω - cm |
| Volume Resistivity (X and Y Axis) | 1x10^12 | Ω - cm |
| Glass Transition Temperature | 100 | °C |
| Coefficient of Thermal Expansion | 50 | Ppm/°C |
| T-Shear Strength | 2100 | psi |
| Weight Loss (at 300°C, TGA) | 2.77 | % |
| Differential Scanning Calorimetry (DSC) Peak Tc | 168 | °C |
| Differential Scanning Calorimetry (DSC) ∆ Hc | -33.4 | J/g |