Creative Materials 124-07
124-07 is a screen-printable, B-Stageable, one part epoxy coating and laminating adhesive. This system features excellent thermal stability, thermal cycle resistance and chemical resistance. Applications include adhesives, printed circuit board fabrication, advanced material composites, sealing, and high performance coatings.\nFeatures\nScreen-print
Product families
Applications
- Printed Circuit Boards (PCBs)
Product Families
- Other Adhesives & Sealants
Other characteristics
- Cure Method
- Heat Cure
- Product Type
- 1K (1 component) Adhesive
- Application Method
- Screen Coating
- Markets
- Electrical & Electronics
- Shelf LIfe
2 months (at 25°C), 3 months at 25°C , 6 months at -10°C
- Cure
- Heat Cure
- Technology
- Ready-to-Use Products
- Procedure
Apply adhesive to substrate. Next apply heat to advance the curing to the non-tacky stage (when cooled to room temperature). A temperature of 125°C for 5 -10 minutes is required (B-Stage time is mass related). User is encouraged to experiment for optimum drying time at a given temperature. Store on release liner to prevent contamination.
- Bonding Procedure
To use, carefully align parts to be bonded, apply uniform pressure to maintain location. Cure for 30 minutes at 175°C, or 1 hour at 150°C. (Note cure times given are mass related. Timing should start after adhesive and substrates reach curing temperature.)
- Safety and Handling
Use with adequate ventilation.; Keep away from sparks and open flames.; Avoid prolonged contact with skin and breathing of vapors.; Wash with soap and water to remove from skin.
- Application Methods
- Screen Coating
- Suggested Handling and Curing
124-07 is a one component system and is ready to use as received. Store frozen to maintain consistent flow properties. Allow material to warm up to room temperature before opening container. Prior to using mix container well. As a coating, cure for one (1) hour at 150°C, or 30 minutes at 175°C. 124-07 can be thinned with small amounts of CMI# 102-03 thinner if needed.
- Ready to Use Product Features
- Chemical Resistant
- Excellent Coating Performance
- Good Thermal Stability
- High Modulus
Technical data
Table 1 of 1
10 rows| Characteristic | Value | Unit |
|---|---|---|
| Viscosity | 25000 | cps |
| Glass Transition Temperature | 105 | °C |
| Lap Shear Strength | 2100 | psi |
| Dielectric Strength | 425 | volts/mil |
| Volume Resistivity | 1x 10^16 | ohm-cm |
| Dielectric Constant (at 100 Hz) | 4 | — |
| Useful Temperature Range | -55 to 230 | ºC |
| Thermal Stability | Good to 325 | °C |
| Coefficient of Thermal Expansion above Tg | 13.5 x 10^-5 | In/in/°C |
| Coefficient of Thermal Expansion above Tg | 29.5 x 10^-6 | In/in/°C |