Creative Materials 114-29A/B
114-29 A/B is a two component, pad printable, radio opaque ink/coating for application by pad printing, dipping and syringe dispensing. The product features excellent adhesion to pretreated polyethylene, and polypropylene, as well as to some varieties of pretreated polytetrafluoroethylene. This material will also adhere to polyurethane, polyamide, melamine, phenolic resins, metal, and glass substrates. Unlike conventional conductive materials, this product is very resistant to abrasion, scratching, flexing and creasing. Some applications for 114-29 A/B include, but are not limited to, manufacturing of medical devices and instruments.\nFeatures
Product families
Applications
- Medical Devices & Assemblies
Product Families
- Functional Inks & Pastes
Other characteristics
- Features
Creasing Resistance, Flexing Resistance, Good Abrasion Resistance, Good Adhesion, Good Scratch Resistance, High Hydrolytic Stability, Radiopaque, Solvent Resistant
- Application Area
- Medical Devices
- Application Method
- Dip Coating, Injection, Pad Printing
- Compatible Substrates & Surfaces
- Glass, Metal
- Markets
- Healthcare & Pharma
- Storage
Shelf life: 6 months at 25°C in original sealed containers. Please note: Part B is sensitive to moisture/humidity and should be tightly re-sealed immediately after using. A purge with nitrogen or other inert gas is recommended for long-term storage.
- Shelf LIfe
- 6 months at 25°C
- Cure
- Heat Cure
- Product Type
- 2K (2 Component) Ink
- Radio Opaque Ink
- Technology
- Ready-to-Use Products
- Suggested Curing
Best properties, for most applications, result when cure with one of the following cure schedules. Good properties can be achieved with a range of cure temperatures from ambient up to 180°C. End user is advised to experimentally determine temperature and time best suited for individual applications.
- Safety and Handling
Contains flammable solvents.; Use with adequate ventilation.; Keep away from sparks and open flames.; Avoid prolonged contact with skin and breathing of vapors.; Wash with soap and water to remove from skin.
- Application Methods
- Dip Coating
- Injection
- Pad Printing
- Suggested Handling
Prior to use, be certain to mix well to re-suspend filler. Mix parts A, and B as prescribed above. Further thinning may be accomplished by adding small amounts of CMI thinners 113-39, 114-20 and/or 127-32R2.
- Certifications and Compliance
- ISO 9001
- Ready to Use Product Features
- Creasing Resistance
- Flexing Resistance
- Good Abrasion Resistance
- Good Adhesion
- Good Scratch Resistance
- High Hydrolytic Stability
- Radiopaque
- Solvent Resistant
- Compatible Substrates and Surfaces
- Glass
- Metal
Technical data
Table 1 of 1
6 rows| Characteristic | Value | Unit |
|---|---|---|
| Viscosity | 12000 | cps |
| Percent Filler (cured) | min. 95 | — |
| Density (Cured) | 9.8 | g/cc |
| Hydrolytic Stability | Excellent | — |
| Useful Temperature Range | -55 to 200 | ºC |
| Pot Life (min. room temperature) | 7 Hrs. | — |