Hauthane L-3632
- CASE Ingredients Features
- Abrasion ResistanceCrack ResistanceExcellent AdhesionLow Temperature Flexibility
- Chemical Family
- Aliphatics, Polyurethanes (PU)AliphaticsPolyurethanes (PU)
Hauthane L-3632 is a medium hard, non-ionic, aliphatic, polyester-based polyurethane dispersion. Features: TEA-free, pyrrolidone-free, APEO-free. Forms medium hard, tough, flexible films. Good abrasion resistance. Superior, low temperature flex-crack resistance. Contains dipropylene glycol monomethyl ether.
Properties
- Physical Form
- Dispersion
Identification
- CASE Ingredients Functions
- Binder & Resin
Product families
Applications
- Textile Manufacturing
Product Families
- Polyurethanes (PU)
Other characteristics
- Brand
- Hauthane
- Features
Abrasion Resistance, Crack Resistance, Excellent Adhesion, Low Temperature Flexibility
- Compatible Substrates & Surfaces
- Fiberglass, Textiles
- Curing
Typical oven drying temperatures and dwell times for aqueous coatings are sufficient to produce optimal film properties.. Do not use crosslinking agents for heat-seal coating applications.
- Carrier
- Polyesters
- Resin-based
- Markets
- Industrial
- Cure
- Heat Cure
- Technology
- CASE Ingredients
- Labeling Claims
- APEO-Free
- Pyrrolidone-free
- TEA-free
- Application Methods
- Spray
- Applications
L-3632 may be used as a sole vehicle or blended with acrylic emulsions.. Viscosity modification can be made with associative thickeners for application by spray, knife-over-roll, or other methods.
- Compatible Substrates and Surfaces
- Fiberglass
- Textiles
Technical data
Table 1 of 2
6 rows| Characteristic | Value | Unit |
|---|---|---|
| Solids | 34 - 36 | % |
| Viscosity | 50 - 500 | cps |
| pH | 4.0 - 7.0 | — |
| Density | 8.7 | lbs/gal |
| Softening Point | 320 | °F |
| VOC Content | 131 | gm/l |
Table 2 of 2
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Elongation | 370 | % | Tested at 20 inches/minute |
| Tensile Strength | 3375 | psi | Tested at 20 inches/minute |
| 100% Modulus | 1040 | psi | Tested at 20 inches/minute |
| 200% Modulus | 1640 | psi | Tested at 20 inches/minute |
| 300% Modulus | 2550 | psi | Tested at 20 inches/minute |