Hauthane HD-6000 DMM (L-2883)
- CASE Ingredients Features
- Chemical ResistanceGood ToughnessHigh GlossHumidity ResistanceWeather Resistance
- Chemical Family
- Polyurethanes (PU)
Hauthane HD-6000 DMM (L-2883) is an NMP-free, APEO-free, polyester-based, hydroxyl-functional, aliphatic, water-borne polyurethane dispersion. Features: Superior chemical resistance. Excellent exterior weathering durability. Excellent humidity resistance. Contains dipropylene glycol dimethylether co-solvent.
Properties
- Physical Form
- Dispersion
Identification
- CASE Ingredients Functions
- Binder & Resin
Product families
Applications
- Consumer Goods — Sports & Recreation
- Vehicle Refinish
- Concrete Coatings & Stains
- Wood Coatings & Finishes
- Vehicle Refinish
- Industrial Maintenance
Product Families
- Polyurethanes (PU)
Other characteristics
- Brand
- Hauthane
- Features
Chemical Resistance, Good Toughness, High Gloss, Humidity Resistance, Weather Resistance
- Compatible Substrates & Surfaces
- Concrete, Metal, Plastics, Wood
- Drying
HD-6000 DMM, crosslinked with a water dispersible isocyanate, will dry to a hard film in 30 minutes at ambient room temperature (65 -+ 70°F) and humidity (RH 50%).; Ultimate cured properties will take 3 -5 days to develop.; If heat is available, the ultimate properties can be attained in shorter time.; Typical oven drying temperatures and dwell times for aqueous coatings are sufficient to produce optimal film properties.
- Carrier
- Water
- Markets
- Automotive & Transportation
- Consumer Goods
- Paints & Coatings
- Technology
- CASE Ingredients
- Labeling Claims
- APEO-Free
- NMP-free
- Application Methods
- Spray
- Applications
HD-6000 DMM crosslinked with water-dispersible isocyanates may be spray applied using single-component equipment.. The workable potlife is approximately 3 hours at the suggested crosslinker ratio of 2.0 to 1.0 NCO / OH.
- Compatible Polymers and Resins
- Acrylics
- Compatible Substrates and Surfaces
- Concrete
- Metal
- Plastics
- Wood
Technical data
Table 1 of 2
7 rows| Characteristic | Value | Unit |
|---|---|---|
| Solids | 34 - 36 | % |
| Viscosity | 50 - 500 | cps |
| pH | 7.5 - 10.0 | — |
| Density | 8.8 | lbs/gal |
| VOC Content | 70 | gm/l |
| OH Equivalent Weight (as supplied) | 3100 | g/l |
| Sward Hardness | 44 | — |
Table 2 of 2
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Elongation | 230 | % | Tested at 20 inches/minute |
| Tensile Strength | 7000 | psi | Tested at 20 inches/minute |
| 100% Modulus | 4850 | psi | Tested at 20 inches/minute |
| 200% Modulus | 6800 | psi | Tested at 20 inches/minute |