Hauthane L-3528
- CASE Ingredients Features
- Abrasion ResistanceExcellent WeatherabilityGood Hydrolysis ResistanceGood ToughnessHigh DurabilityHumidity ResistanceOxidation ResistantUV Resistance
- Chemical Family
- Polyurethanes (PU)
Hauthane L-3528 is a co-solvent free, polycarbonate-based, aliphatic, polyurethane dispersion. Features: Excellent exterior weathering durability. Excellent humidity resistance. Outstanding toughness and abrasion-resistance. Co-solvent frec, tin-free, APEO-free.
Properties
- Physical Form
- Dispersion
Identification
- CASE Ingredients Functions
- Binder & Resin
Product families
Applications
- Architectural Coatings
- Wood Coatings & Finishes
- Architectural Coatings
- Floor Coatings
- Industrial Maintenance
- Metal Coatings
Product Families
- Polyurethanes (PU)
Other characteristics
- Brand
- Hauthane
- End Uses
- Wood Coating
- Features
Abrasion Resistance, Excellent Weatherability, Good Hydrolysis Resistance, Good Toughness, High Durability, Humidity Resistance, Oxidation Resistant, UV Resistance
- Compatible Substrates & Surfaces
Acrylonitrile Butadiene Styrene (ABS), Metal, Plastics, Polycarbonate (PC), Wood
- Curing
L-3528 may be air dried, if desired, depending on film thickness. The addition of 5 - 10% coalescing solvent is suggested in ambient temperature drying situations. Typical oven drying temperatures and dwell times for aqueous coatings may be sufficient to produce optimal film properties..
- Markets
- Building & Construction
- Paints & Coatings
- Cure
- Air Dry
- Coating Type
- Wood Coating
- Technology
- CASE Ingredients
- Suggested Uses
L-3528 was developed for general coatings use on wood, plastic and metal substrates. The product offers exceptional resistance to hydrolysis, oxidation and UV-degradation. L-3528 is ideally suited for exterior applications where film durability and longevity are important considerations.
- Labeling Claims
- APEO-Free
- Cosolvent-free
- Tin-free
- Application Methods
- Brush
- Padding
- Spray
- Application
L-3528 may be formulated into coatings applied by spray, brush or pad applicator. It can be used as a sole vehicle or blended with acrylic emulsions. The rheology may be modified with associative thickeners.
- Characteristics
- Excellent exterior weathering durability
- Excellent humidity resistance
- Outstanding toughness and abrasion-resistance
- Co-solvent free, tin-free, APEO-free
- Compatible Polymers and Resins
- Acrylics
- Polyvinyl Chloride (PVC)
- Compatible Substrates and Surfaces
- Acrylonitrile Butadiene Styrene (ABS)
- Metal
- Plastics
- Polycarbonate (PC)
- Wood
Technical data
Table 1 of 2
6 rows| Characteristic | Value | Unit |
|---|---|---|
| Solid Content | 34 - 36 | % |
| Viscocity | 50 - 500 | cPs |
| pH | 7.5 - 10.0 | — |
| Density | 1.06 | — |
| Volatile Organic Compounds (less water) | 12.0 | g/l |
| Volatile Organic Compounds (as supplied) | 41.0 | g/l |
Table 2 of 2
5 rows| Characteristic | Value | Unit |
|---|---|---|
| Elongation (at 20 inch/min) | 340.0 | % |
| Tensile Strength (at 20 inch/min) | 4400.0 | psi |
| 100% Modulus (at 20 inch/min) | 2040.0 | psi |
| 200% Modulus (at 20 inch/min) | 2700.0 | psi |
| 300% Modulus (at 20 inch/min) | 3800.0 | psi |