Hauthane HD-4664
- CASE Ingredients Features
- Abrasion ResistanceCrack ResistanceGood ToughnessImproved FlexibilityLow Temperature Flexibility
- Chemical Family
- Polyurethanes (PU)
Hauthane HD-4664 is a medium soft, high solids, co-solvent free, aliphatic, polyurethane dispersion. Features: High solids (50%). Contains no co-solvent. Medium soft, tough, dry film. Superior abrasion resistance. Exceptional low temperature flexibility and crack resistance.
Properties
- Physical Form
- Dispersion
Identification
- CASE Ingredients Functions
- Binder & Resin
Product families
- Polyurethanes (PU)
Other characteristics
- Brand
- Hauthane
- End Uses
- Base Coat, Solventless & High Solids Coating
- Features
Abrasion Resistance, Crack Resistance, Good Toughness, Improved Flexibility, Low Temperature Flexibility
- Compatible Substrates & Surfaces
- Leather, Textiles
- Curing
HD-4664 can be air dried, if desired, depending on film thickness. Typical drying temperatures and dwell times for aqueous coatings are sufficient to produce optimal film properties..
- Carrier
- Water
- Coating Type
- Base Coat
- Solventless & High Solids Coating
- Technology
- CASE Ingredients
- Suggested Uses
HD-4664 was designed as a high solids, multi-purpose textile binder polymer. It may be used as a blending resin for harder polyurethane polymers to impart greater film flexibility. A balanced composition provides good stability with acrylic latices and confers superior strength, abrasion resistance and low temperature flexibility properties.
- Labeling Claims
- Cosolvent-free
- Application Methods
- Knife-over-roll
- Padding
- Spray
- Application
HD-4664 can be used as a sole vehicle or blended with acrylic emulsions for spray or pad bath applications. Solids can be reduced with water to optimize dry coating weight. This product may also be thickened with associative thickeners for knife-over-roll or similar methods.
- Characteristics
High solids (50%); Contains no co-solvent; Medium soft, tough, dry film; Superior abrasion resistance; Exceptional low temperature flexibility and crack resistance
- Compatible Polymers and Resins
- Acrylics
- Compatible Substrates and Surfaces
- Leather
- Textiles
Technical data
Table 1 of 2
7 rows| Characteristic | Value | Unit |
|---|---|---|
| Solid Content | 49 - 51 | % |
| Viscocity | 200 - 800 | cPs |
| pH | 7.5 - 10.0 | — |
| Density | 8.8 | lbs/gal |
| Softening Point | 310.0 | °F |
| Volatile Organic Compounds (as supplied) | 12.0 | g/l |
| Sward Hardness | 14.0 | — |
Table 2 of 2
5 rows| Characteristic | Value | Unit |
|---|---|---|
| Elongation (at 20 inch/min) | 625.0 | % |
| Tensile Strength (at 20 inch/min) | min. 6000 | psi |
| 100% Modulus (at 20 inch/min) | 800.0 | psi |
| 200% Modulus (at 20 inch/min) | 1100.0 | psi |
| 300% Modulus (at 20 inch/min) | 1500.0 | psi |