Hauthane L-3614 Polyurethane Dispersions
- CASE Ingredients Features
- Abrasion ResistanceCrack ResistanceGood ToughnessLow Temperature FlexibilityUV Resistance
- Chemical Family
- Aliphatics, Polyurethanes (PU)AliphaticsPolyurethanes (PU)
Hauthane L-3614 is a very soft, co-solvent free, aliphatic, polyester polyurethane dispersion. Features: Co-solvent free, TEA free, Tin free, APEO free. Ultra soft, tough, dry film. Very good abrasion and UV resistance. Exceptional low temperature flexibility and crack resistance.
Properties
- Physical Form
- Dispersion
Identification
- CASE Ingredients Functions
- Binder & Resin
Product families
Applications
- Textile Manufacturing
Product Families
- Polyurethanes (PU)
Other characteristics
- Brand
- Hauthane
- Features
Abrasion Resistance, Crack Resistance, Good Toughness, Low Temperature Flexibility, UV Resistance
- Compatible Substrates & Surfaces
- Textiles
- Curing
L-3614 can be air dried, if desired, depending on film thickness.. Typical drying temperatures and dwell times for aqueous coatings are sufficient to produce optimal film properties.
- Markets
- Industrial
- Cure
- Air Dry
- Product Uses
It may be used as a blending resin with the harder L-3615 to impart increased toughness.. A balanced composition provides good stability with acrylics and confers superior strength, abrasion resistance and low temperature flexibility properties.
- Technology
- CASE Ingredients
- Labeling Claims
- APEO-Free
- Solvent-free
- TEA-free
- Tin-free
- Application Methods
- Spray
- Applications
L-3614 can be used as a sole vehicle or blended with other coatings for spray or pad bath applications. Solids can be adjusted with water to optimize dry coating weight. This product may also be thickened with associative thickeners for knife-over-roll or similar methods
- Compatible Substrates and Surfaces
- Textiles
Technical data
Table 1 of 2
6 rows| Characteristic | Value | Unit |
|---|---|---|
| Solids | 34 - 36 | % |
| Viscosity | 50 - 500 | cps |
| pH | 7.5 - 10.0 | — |
| Density | 8.8 | lbs/gal |
| Softening Point | 290 | °F |
| VOC Content (less water) | 47 | gm/l |
Table 2 of 2
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Elongation | 810 | % | Tested at 20 inches/minute |
| Tensile Strength | 5760 | psi | Tested at 20 inches/minute |
| 100% Modulus | 1050 | psi | Tested at 20 inches/minute |
| 200% Modulus | 1320 | psi | Tested at 20 inches/minute |
| 300% Modulus | 1620 | psi | Tested at 20 inches/minute |