Hauthane L-3615 is a hard, co-solvent free, aliphatic, polyester polyurethane dispersion. Features: Co-solvent free, TEA free, Tin free, APEO free. Medium hard, tough, dry film. Excellent water and chemical resistance. Superior abrasion resistance. Good adhesion to a wide variety of substrates.
Properties
- Physical Form
- Dispersion
Identification
- CASE Ingredients Functions
- Binder & Resin
Product families
Applications
- Consumer Goods — Furniture
- Architectural Coatings
- Concrete Coatings & Stains
- Wood Coatings & Finishes
- Architectural Coatings
- Metal Coatings
Product Families
- Polyurethanes (PU)
Other characteristics
- Brand
- Hauthane
- End Uses
- Top Coat, Varnishes, Wood Coating
- Features
Abrasion Resistance, Chemical Resistance, Good Toughness, Improved Flexibility, Improves Adhesion, Low Temperature Flexibility, Water Resistance
- Compatible Substrates & Surfaces
- Concrete, Metal, Plastics, Wood
- Curing
L-3615 can be air dried, if desired, depending on film thickness. Typical drying temperatures and dwell times for aqueous coatings are sufficient to produce optimal film properties..
- Markets
- Building & Construction
- Consumer Goods
- Paints & Coatings
- Cure
- Air Dry
- Coating Type
- Top Coat
- Varnishes
- Wood Coating
- Technology
- CASE Ingredients
- Suggested Uses
L-3615 was designed for topcoat applications on a wide variety of substrates, including concrete, metal, plastic and wood. It may also be used as a blending resin with the softer L-3614 to impart greater film flexibility. A balanced composition provides good stability with acrylics and confers superior strength, abrasion resistance and low temperature flexibility properties.
- Labeling Claims
- APEO-Free
- Cosolvent-free
- TEA-free
- Tin-free
- Application Methods
- Knife-over-roll
- Padding
- Spray
- Application
L-3615 can be used as a sole vehicle or blended with other coatings for spray or pad bath applications. Solids can be adjusted with water to optimize dry coating weight. This product may also be thickened with associative thickeners for knife-over-roll or similar methods.
- Characteristics
- Co-solvent free, TEA free, Tin free, APEO free
- Medium hard, tough, dry film
- Excellent water and chemical resistance
- Superior abrasion resistance
- Good adhesion to a wide variety of substrates
- Compatible Polymers and Resins
- Acrylics
- Compatible Substrates and Surfaces
- Concrete
- Metal
- Plastics
- Wood
Technical data
Table 1 of 2
6 rows| Characteristic | Value | Unit |
|---|---|---|
| Solid Content | 34 - 36 | % |
| Viscocity | 50 - 500 | cPs |
| pH | 7.5 - 10.0 | — |
| Density | 8.8 | lbs/gal |
| Softening Point | 360.0 | °F |
| Volatile Organic Compounds (less water) | 45.0 | g/l |
Table 2 of 2
4 rows| Characteristic | Value | Unit |
|---|---|---|
| Elongation (at 20 inch/min) | 260.0 | % |
| Tensile Strength (at 20 inch/min) | min. 6000 | psi |
| 100% Modulus (at 20 inch/min) | 4300.0 | psi |
| 200% Modulus (at 20 inch/min) | 5500.0 | psi |