Hauthane HD-2313
- CASE Ingredients Features
- Cost EffectiveCrack ResistanceGood ToughnessImproved Flexibility
- Chemical Family
- Polyurethanes (PU)
Hauthane HD-2313 is a co-solvent free, flame retardant, aliphatic, aqueous polyurethane dispersion. Features: Permanent, non-leaching flame retardancy. Contains no co-solvent. Excellent cost/performance ratio. Soft, tough, flexible, dry film. Excellent low temperature flex crack resistance.
Properties
- Physical Form
- Dispersion
Identification
- CASE Ingredients Functions
- Binder & ResinFlame Retardant
Product families
- Functional Additives
- Polyurethanes (PU)
Other characteristics
- Brand
- Hauthane
- Labeling Claims
- Cosolvent-free, Solvent-free
- Cosolvent-free
- Solvent-free
- Compatible Substrates & Surfaces
- Textiles
- Curing
This product displays excellent strength properties as supplied, although melamine-formaldehyde (3-6 phr) may be added to enhance performance..
- Markets
- Consumer Goods
- Applications
- Consumer Goods — Carpet & Upholstery
- Coating Type
- Solventless & High Solids Coating
- Technology
- CASE Ingredients
- Suggested Uses
HD-2313 was designed for use as a coating or finish for synthetic textile fabrics that must have permanent flame retardancy. This unique urethane dispersion is manufactured at high solids and without the use of solvent. Low add-on levels of HD-2313 will enable synthetic fabrics to pass various FR tests including NFPA-701, MVSS-302, & others. HD-2313 is well suited for use in textile coatings, such as automotive upholstery, that require outstanding strength and fire retardancy without the use of antimony-oxide/decabrome chemistry. Using HD-2313, a coating can be formulated to pass MVSS-302 and maintain required strength properties at a much lower coating weight than conventional coatings. This results in a much softer hand and possible cost savings. The high solids and solvent-free nature of HD-2313 make it a very cost effective urethane.
- Application Methods
- Padding
- Spray
- Application
HD-2313 may be sprayed or pad applied as supplied. It may be thickened for alternative application methods.
- Characteristics
- Permanent, non-leaching flame retardancy
- Contains no co-solvent
- Excellent cost/performance ratio
- Soft, tough, flexible, dry film
- Excellent low temperature flex crack resistance
- Compatible Substrates and Surfaces
- Textiles
Technical data
Table 1 of 2
6 rows| Characteristic | Value | Unit |
|---|---|---|
| Solid Content | 44 - 46 | % |
| Viscocity | 50 - 500 * | cPs |
| pH | 6.5 - 9.5 | — |
| Density | 8.8 | lbs/gal |
| Softening Point | 320.0 | °F |
| Volatile Organic Compounds | 0.8 | %/wt |
Table 2 of 2
5 rows| Characteristic | Value | Unit |
|---|---|---|
| Elongation (at 20 inch/min) | 560.0 | % |
| Tensile Strength (at 20 inch/min) | min. 3500 | psi |
| 100% Modulus (at 20 inch/min) | 560.0 | psi |
| 200% Modulus (at 20 inch/min) | 720.0 | psi |
| 300% Modulus (at 20 inch/min) | 880.0 | psi |