Hauthane HD-2334
- CASE Ingredients Features
- Crack ResistanceGood ToughnessHigh Melting PointImproved FlexibilityLow Temperature FlexibilityUV Resistance
- Chemical Family
- Polyurethanes (PU)
Hauthane HD-2334 is co-solvent free, high solids, flame-retardant, aliphatic, polyurethane dispersion. Features: Permanent, non-leaching flame-retardancy. Contains no co-solvent. Good UV resistance. Stiff, tough, flexible, dry film. High melting point (340°F). Good low temperature flexibility and crack resistance.
Properties
- Physical Form
- Dispersion
Identification
- CASE Ingredients Functions
- Binder & ResinFlame Retardant
Product families
- Functional Additives
- Polyurethanes (PU)
Other characteristics
- Brand
- Hauthane
- Labeling Claims
- Cosolvent-free
- Compatible Substrates & Surfaces
- Textiles
- Curing
HD-2334 may be air-dried. Typical drying temperatures and dwell times for aqueous coatings are sufficient to produce optimal film properties. Enhanced properties may be attained through the use of various crosslinkers..
- Cure
- Air Dry
- Coating Type
- Solventless & High Solids Coating
- Technology
- CASE Ingredients
- Suggested Uses
HD-2334 was designed for use as a coating or finish for synthetic textile fabrics that must have permanent flame-retardancy. Low add-on levels of HD- 2334 will enable synthetic fabrics to pass various FR tests including NFPA- 701, MVSS-302 and others. The film properties of HD-2334 also provide a stiff hand and excellent molding/pleating properties. Due to its aliphatic composition, excellent UV resistance is also exhibited.
- Application Methods
- Padding
- Spray
- Application
Spray or pad -- solids may be adjusted for optimum add-on. May be thickened with HA-900 for alternative application methods.
- Characteristics
Permanent, non-leaching flame-retardancy; Contains no co-solvent; Good UV resistance; Stiff, tough, flexible, dry film; High melting point (340°F); Good low temperature flexibility and crack resistance
- Compatible Substrates and Surfaces
- Textiles
Technical data
Table 1 of 2
6 rows| Characteristic | Value | Unit |
|---|---|---|
| Solid Content | 44 - 46 | % |
| Viscocity | 50 - 500 | cPs |
| pH | 6.5 - 9.5 | — |
| Density | 9.1 | lbs/gal |
| Softening Point | 340.0 | °F |
| Volatile Organic Compounds (as supplied) | 12.0 | g/l |
Table 2 of 2
4 rows| Characteristic | Value | Unit |
|---|---|---|
| Elongation (at 2 inch/min) | 245.0 | % |
| Tensile Strength (at 2 inch/min) | 3750.0 | psi |
| 100% Modulus (at 2 inch/min) | 2600.0 | psi |
| 200% Modulus (at 2 inch/min) | 3250.0 | psi |