Hauthane L-3360
- CASE Ingredients Features
- Abrasion ResistanceCrack ResistanceGood ToughnessLow Temperature FlexibilityUV Resistance
- Chemical Family
- Polyurethanes (PU)
Hauthane L-3360 is a partially bio-renewable resource based, NMP-free, soft, aliphatic, waterborne, polyurethane dispersion. Features: 50% bio-based, renewable resource content. Superior flexibility. Produce soft, tough, flexible, dry films. Good UV resistance. Very good abrasion resistance. Superior low temperature flexibility and crack resistance. Contains n-cthyl pyrrolidone (NEP).
Properties
- Physical Form
- Dispersion
Identification
- CASE Ingredients Functions
- Binder & Resin
Product families
Applications
- Leather Manufacturing
- Textile Manufacturing
Product Families
- Polyurethanes (PU)
Other characteristics
- Brand
- Hauthane
- End Uses
- Top Coat
- Features
Abrasion Resistance, Crack Resistance, Good Toughness, Low Temperature Flexibility, UV Resistance
- Compatible Substrates & Surfaces
- Fibers & Fabrics, Leather, Textiles
- Curing
The product exhibits good strength properties as supplied, but may be crosslinked with carbodiimide (ambient temperature conditions) and melamine-formaldehyde (high temperature conditions) crosslinkers to improve performance.
- Carrier
- Water
- Markets
- Industrial
- Coating Type
- Top Coat
- Product Uses
L-3360 was designed for use in textile applications as a versatile polyurethane coating.; Due to its overall properties, L-3360 can be used as a finish or a coating for many textile applications.; This product is ideally suited for use as an anti-fray finish on textile fabrics that must have a soft hand.; L-3360 is also suitable for textile coating applications that require excellent low temperature flexibility and crack resistance.
- Technology
- CASE Ingredients
- Labeling Claims
- NMP-free
- Application Methods
- Air Knife Coating
- Pad Printing
- Spray
- Applications
Spray or pad, solids may be adjusted for optimum add-on.; Formulas may be thickened with rheology modifiers for knife coating applications.
- Compatible Substrates and Surfaces
- Fibers & Fabrics
- Leather
- Textiles
Technical data
Table 1 of 2
5 rows| Characteristic | Value | Unit |
|---|---|---|
| Solids | 34 - 36 | % |
| Viscosity | 50 - 500 | cps |
| pH | 7.5 - 10.0 | — |
| Density | 8.5 | lbs/gal |
| VOC Content (less water) | 55 | gm/l |
Table 2 of 2
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Elongation | 370 | % | Tested at 20 inches/minute |
| Tensile Strength | 1600 | psi | Tested at 20 inches/minute |
| 100% Modulus | 700 | psi | Tested at 20 inches/minute |
| 200% Modulus | 950 | psi | Tested at 20 inches/minute |
| 300% Modulus | 1300 | psi | Tested at 20 inches/minute |