AFT Fluorotec AF1008 U203-D57G
- Chemical Family
- Polyurethanes (PU)
AFT Fluorotec AF1008 U203-D57G is a hydrolysis resistant PU (H-PU) composed of prepolymers based on polyoxytetrametylene glycol (PTMEG) and diphenylmethane diisocyanate (MDI) processed liquid with catalysts and a MoS2 polyol. The hardness is adjusted at 57 +/-2 Shore D which makes it an excellent extrusion resistant material. This special MoS2 composition performs excellent in critical lubrication situations and reducing the stick-slip behavior.
Product families
Applications
- Chassis & Brake
- Exterior & Body
- Fuel Systems
- Interior
- Other Automotive Applications
- Powertrain & UTH
- Equipment & Parts
- Other Industrial Applications
Product Families
- Polyurethane Rubbers
Other characteristics
- End Uses
Automotive Applications, Automotive Interior Parts, Conveyors, Fuel Pump Modules, Gaskets, Hydraulic Applications, Machine/Mechanical Parts, Seals, Steering Bellows
- Features
Extrusion Resistance, Hydrolysis Resistant, Improves Stick-Slip Response
- Polymer Name
- Polyurethane Thermoset Elastomer (unspecified)
- Markets
- Automotive & Transportation
- Industrial
- Technology
- Elastomers
- Main Application
Seals and composite seals (with rubber preload element), wipers, back-up rings, low friction and wear, high extrusion resistance, compatibility with water, excellent low temp. characteristics.
- Additives Included
- Lubricant (Molybdenum Disulfide)
- Material Features
- Extrusion Resistance
- Hydrolysis Resistant
- Improves Stick-Slip Response
- Analysis and Evaluation
The properties relate to fundamental values for polyurethane products. Values mentioned above are corresponding to ASTM or DIN standard and have been tested on standardized plates in the laboratory. All immersion tests are made under laboratory conditions.
- Plastics and Elastomers End Uses
- Automotive Applications
- Automotive Interior Parts
- Conveyors
- Fuel Pump Modules
- Gaskets
- Hydraulic Applications
- Machine/Mechanical Parts
- Seals
Technical data
Table 1 of 1
11 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 1,13 | g/cm3 | DIN 53479 |
| Modulus | min. 18 | N/mm2 | DIN 53504 |
| Tensile strength | min. 30 | N/mm2 | DIN 53504 |
| Elongation at break | min. 330 | % | DIN 53504 |
| Tear strength | 125.0 | KN/m | DIN 53515 |
| Rebound resilience | 42.0 | % | DIN 53512 |
| Compression set | 32.0 | % | DIN 53517 |
| Hardness at -5°C | 57.0 | Shore D | DIN 53505 |
| Hardness at +80°C | 52.0 | Shore D | DIN 53505 |
| Service temperature | min. -30 | °C | — |
| Service temperature | max. 90 | °C | — |