ResinLab® EP1026 Black Part A
Resinlab® EP1026 Black Part A is a two-part, unfilled epoxy adhesive designed for high speed bonding of metals, ceramics, and most plastics. It cures to a tough semi-rigid material and is free-flowing in viscosity. It gives good resistance to water, salt spray, inorganic acids and bases, and most organic solvents. EP1026 Black was formulated to a 1A:1B by volume mix ratio for use in either meter/mix and dispense equipment or side-by-side dual cartridges for easy dispensing. Handling cure is normally achieved at room temperature within 20-30 minutes with full cure in 24 hours. Because of the fast and exothermic reaction process, this product should only be used in small volumes.
Product families
Ready-to-Use Products — Adhesives & Sealants
- Other Adhesives & Sealants
Other characteristics
- Brand
- ResinLab
- Cure Method
- Air Dry
- Product Type
- 2K (2 component) Adhesive, Epoxy Adhesive
- 2K (2 component) Adhesive
- Epoxy Adhesive
- Compatible Substrates & Surfaces
- Ceramic, Metal, Plastics
- Color
- Black
- Markets
- Adhesives & Sealants
- Cure
- Air Dry
- Applications
Adhesives & Sealants — Other Adhesives & Sealants Applications
- Technology
- Ready-to-Use Products
- Ready to Use Product Features
- Chemical Resistant
- Excellent Salt Spray Resistance
- Free Flowing
- Water Resistant
- Compatible Substrates and Surfaces
- Ceramic
- Metal
- Plastics
Technical data
Table 1 of 1
34 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Mix Ratio | Part A to Part B | — | — |
| Dissipation Factor (at 100 Hz) | 0.008 | — | ASTM D150 |
| Dissipation Factor (at 100 Hz) | 0.02 | — | ASTM D150 |
| Mix Ratio (By Weight) | 1.03:1 | — | — |
| Mix Ratio (By Volume) | 1:1 | — | — |
| Cure Schedule (at 25°C) | 24.0 | h | — |
| Viscosity (Part A,Rheometer parallel plate 25mm at 1/s) | 15500.0 | cps | — |
| Viscosity (Part B,Rheometer parallel plate 25mm at 1/s) | 16000.0 | cps | — |
| Viscosity (Mixed Rheometer parallel plate 25mm at 1/s) | 15500.0 | cps | — |
| Specific Gravity (Part A) | 1.16 | — | — |
| Specific Gravity (Part B) | 1.12 | — | — |
| Specific Gravity (Mixed) | 1.14 | — | — |