Crosslink Technologies CLH6010
- Chemical Family
- Epoxy & Epoxy Derivatives
Crosslink Technologies CLH6010 is a low stress, extremely tough casting compound which was developed for casting low voltage bushings and insulators.
Product families
Applications
Applications
- Electrical & Electronics — Other Electrical & Electronics Applications
Electrical & Electronics — Packaging & Assembly
- Potting Compounds
Electrical & Electronics — Wire & Cable
- Jacketing & Insulation
Product Families
Plastics — Thermoset Resins
- Epoxies
Other characteristics
- End Uses
Bushings, Electrical Components, Electrical/Electronic Applications, Encapsulant, Low Voltage Insulation
- Polymer Name
- Epoxy Resins & Compounds
- Processing Methods
- Casting
- Volume Resistivity
- 4300000000000.0 - 4300000000000.0 Ohm-m
- Markets
- Electrical & Electronics
- Shelf LIfe
- 12 Months
- Cure
- Air Dry
- Technology
- Plastics
- Cure Schedule
- Recommended Cure Schedule at 22 °C - 24 Hrs
- Alternate Cure Schedule at 60 °C - 4 Hrs.
- Material Features
- Electrically Insulating
- Plastics and Elastomers End Uses
- Bushings
- Electrical Components
- Electrical/Electronic Applications
- Encapsulant
- Low Voltage Insulation
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Casting
Technical data
Table 1 of 4
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Viscosity at 70°C | 200 - 400 | cps |
| Specific Gravity | 1 - 1.04 | g/cm³ |
Table 2 of 4
6 rows| Characteristic | Value | Unit |
|---|---|---|
| Dielectric Constant at 10 KHz | 4.06 | — |
| Dielectric Constant at 1 KHz | 3.86 | — |
| Dissipation Factor at 10 KHz | 0.0197 | — |
| Dissipation Factor at 1 KHz | 0.0178 | — |
| Dielectric Strength (62 Mil/Section) | 594 | Volts/Mil |
| Volume Resistivity | 4.3 x10^14 | Ohm/Cm |
Table 3 of 4
13 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 1.75 | gm/Cm³ | — |
| Hardness | 91 | Shore D | — |
| Guide To Operating Temperature | 130 | °C | — |
| Linear Shrinkage | 0.0065 | In/In | Astm D 2566 |
| Tensile Strength | 10500 | Psi | Astm D 638 |
| Tensile Elongation | 4.5 | % | Astm D 638 |
| HDT | 117 | °C | Astm D 648 |
| Coefficient of Thermal Expansion | 43 x10^-6 | in/in/°C | — |
| Thermal Conductivity | 37X10^-4 | Cal/Sec.Cm.°C | — |
| Moisture Absorption | 0.04 | % | — |
| Flextural Strength | 16000 | Psi | — |
| Flextural Modulus | 11,00,000 | Psi | — |
Table 4 of 4
4 rows| Characteristic | Value | Unit |
|---|---|---|
| Mix Ratio By Weight | 100:7.5 | — |
| Mixed Viscosity at 70°C | 4500 | cps |
| Pot Life Of 200 gm. mass at 70°C | 4 | minutes |
| Gel Time Of 200 gm. mass at 70°C | 6 | minutes |