Crosslink Technologies CLH6441
- Chemical Family
- Epoxy & Epoxy Derivatives
Crosslink Technologies CLH6441 is a filled, room temperature cure, two component epoxy system. The system is suitable for potting and encapsulating electrical and electronic components. The products use of non-abrasive filler and convenient mix ratio makes it suitable for processing in automatic dispense equipment. This product is certified with ul and passes ul94-v1 flammability testing.
Product families
Applications
Applications
- Electrical & Electronics — Other Electrical & Electronics Applications
Electrical & Electronics — Packaging & Assembly
- Potting Compounds
Electrical & Electronics — Wire & Cable
- Jacketing & Insulation
Product Families
Plastics — Thermoset Resins
- Epoxies
Other characteristics
- End Uses
Electrical Components, Electrical/Electronic Applications, Encapsulant
- Polymer Name
- Epoxy Resins & Compounds
- Processing Methods
- Casting, Potting
- Volume Resistivity
- 40000000000000.0 - 40000000000000.0 Ohm-m
- Markets
- Electrical & Electronics
- Shelf LIfe
- 12 Months
- Cure
- Air Dry
- Flame Rating
- UL 94 V1
- Technology
- Plastics
- Cure Schedule
- Recommended Cure Schedule at 22 °C - 24 Hrs
- Alternate Cure Schedule at 60 °C - 6 Hrs.
- Certifications and Compliance
- UL 94
- Plastics and Elastomers End Uses
- Electrical Components
- Electrical/Electronic Applications
- Encapsulant
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Casting
- Potting
Technical data
Table 1 of 4
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Viscosity | 16,000 - 20,000 | cps |
| Specific Gravity | 1.55 - 1.61 | g/cm³ |
Table 2 of 4
4 rows| Characteristic | Value | Unit |
|---|---|---|
| Dielectric Constant at 1 KHz | 4 | — |
| Dissipation Factor at 1 KHz | 0.02 | — |
| Dielectric Strength (62 Mil/Section 150 Seconds) | 400 | Volts/Mil |
| Volume Resistivity | 40 x10^14 | Ohm/Cm |
Table 3 of 4
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 1.59 | gm/Cm³ | — |
| Hardness | 87 | Shore D | — |
| Linear Shrinkage | 0.004 | In/In | Astm D 2566 |
| Tensile Strength | 5500 | Psi | Astm D 638 |
| Tensile Elongation | 4 | % | Astm D 638 |
| HDT | 52 | °C | Astm D 648 |
| Flammability | UL94-V1 | Cal/Sec.Cm.°C | — |
Table 4 of 4
4 rows| Characteristic | Value | Unit |
|---|---|---|
| Mix Ratio By Weight (by vol. 100:100.0) | 100:100.0 | — |
| Mixed Viscosity at 22°C | 21000 | cps |
| Pot Life Of 200 gm. mass at 22°C | 20 | minutes |
| Gel Time Of 200 gm. mass at 22°C | 45 | hours |