MXBON® LIGHT CURE CYANOACRYLATE 22446
MXBON® LIGHT CURE CYANOACRYLATE 22446 is a odorless light-curing cyanoacrylate adhesive. It is designed for bonding applications that require very rapid fixture, filet cure or surface cure. The UV and visible light cure properties facilitated rapid curing of exposed surface area and makes it a unique product in the world of light-curing adhesive.
Properties
- Physical Form
- Liquid
Product families
- Contact Adhesives
Other characteristics
- Brand
- MXBON
- Cure Method
- Moisture Cure, Radiation Cure
- Product Type
- 1K (1 component) Adhesive, Anaerobic Adhesive
- 1K (1 component) Adhesive
- Anaerobic Adhesive
- Cure
- Ultraviolet (UV) light
- Moisture Cure
- Radiation Cure
- Color
- Transparent
- Markets
- Adhesives & Sealants
- Industrial
- Chemistry
- Alkoxyethyl Cyanoacrylate with photoinitiator
- Viscosity
- Medium
- Appearance
- Transparent, yellow liquid
- Components
- One part requires no mixing
- Technology
- Cyanoacrylate / UV / Visible
- Ready-to-Use Products
- Conversions
(ºC x 1.8) + 32 = ºF kV/mm x 25.4 = V/mil mm / 25.4 = in μm / 25.4 = mil N x 0.225 = lb N/mm x 5.71 = lb/in N/mm2 x 145 = psi MPa x 145 = psi N·m x 8.851 = lb·in N·mm x 0.142 = oz·in mPa·s = cP
- Secondary Cure
- Humidity
- General Information
This product is not recommended for use in pure oxygen and/or oxygen rich systems and should not be selected as a sealant for chlorine or other strong oxidizing materials. For safe handling information on this product, consult the Safety Data Sheet (SDS): Directions for use: 1) This product is light sensitive; exposure to daylight, UV light and artificial light should be kept to a minimum during storage and handling. 2) For best performance bond surfaces should be clean and free from grease. 3) This product performs best in thin bond gaps (0.05 mm) 4) Excess adhesive can be dissolved with nitromethane or acetone.
- Typical Performance
TACK FREE TIME Tack Free Time is the time in seconds required to achieve a tack free surface. UV/Visible Light Sources: Electrodeless, V bulb: 70 mW/cm2, measured @ 365 nm: < 10 s. Electrodeless, H bulb: 30 mW/cm2, measured @ 365 nm: < 10 s. 100 mW/cm2, measured @ 365 nm: < 10 s. Visible Light Sources: Blue light laser: 70 mW/cm2, measured @ 445 nm: < 10 s. CURE SPEED vs. SUBSTRATE (non-UV/Vis cure) The rate of cure will depend on the substrate used. The table below shows the fixture time achieved on different materials at room temperature. This is defined as the time at which an adhesive bond (250 mm 2 ) is capable of su pporting a 3 kg load for 10 seconds. Fixture time measurements relate to non UV/Visible cure.
Technical data
Table 1 of 1
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Specific Gravity (25°C) | 1.13 | g/cm³ |
| Viscosity (25°C) | 600 - 1200 | mPa. s |